Amorphous crystallinity

When drawdown is high, the film may be uniaxially oriented and the properties of the final film isotropic. In the manufacture of strapping tape this effect is accentuated. If the cast or quenched film is to be used to feed an orientation tine, additional attention must be given to the amorphous—crystalline nature of the film ia the draw processes so that maximum strength can be achieved and uniform gauge and optical quality maintained. Slot casting is used for the orientation of these resins, polyesters, polyamides, and a variety of others. 

To erase information by the transition amorphous — crystalline, the amorphous phase of the selected area must be crystallized by annealing. This is effected by illumination with a low power laser beam (6—15 mW, compared to 15—50 mW for writing/melting), thus crystallizing the area. This crystallization temperature is above the glass-transition point, but below the melting point of the material concerned (Eig. 15, Erase). 

In order for a plasticizer to enter a polymer stmcture the polymer should be highly amorphous. Crystalline nylon retains only a small quantity of plasticizer if it retains its crystallinity. Once it has penetrated the polymer the plasticizer fills free volume and provides polymer chain lubrication, increa sing rotation and movement. 

Stannous Oxide Hydrate. Stannous oxide hydrate [12026-24-3] SnO H2O (sometimes erroneously called stannous hydroxide or stannous acid), mol wt 152.7, is obtained as a white amorphous crystalline product on treatment of stannous chloride solutions with alkaH. It dissolves in alkaH solutions, forming stannites. The stannite solutions, which decompose readily to alkaH-metal stannates and tin, have been used industrially for immersion tinning. 

Anodic oxidation (barrier films) Amorphous + crystalline AI2O3 + anions of solution 1000-3000... 

The preparation and properties of a novel, commercially viable Li-ion battery based on a gel electrolyte has recently been disclosed by Bellcore (USA) [124]. The technology has, to date, been licensed to six companies and full commercial production is imminent. The polymer membrane is a copolymer based on PVdF copolymerized with hexafluoropropylene (HFP). HFP helps to decrease the crystallinity of the PVdF component, enhancing its ability to absorb liquid. Optimizing the liquid absorption ability, mechanical strength, and processability requires optimized amorphous/crystalline-phase distribution. The PVdF-HFP membrane can absorb plasticizer up to 200 percent of its original volume, especially when a pore former (fumed silica) is added. The liquid electrolyte is typically a solution of LiPF6 in 2 1 ethylene carbonate dimethyl car-... 

Sacrifice (from Base Resin) Amorphous Crystalline... 

Define the terms rubbery amorphous, glassy amorphous, crystalline and semicrystalline. 

The quality of the polymer, its photo-oxidation and thermo-oxidation history expressed in concentration of hydroperoxides, carbonyl groups or of other oxidized structures and terminal groups. The rate of an oxidative attack may then be related to the average molar mass and to its distribution, and to the ratio of amorphous/crystalline structures. Polymers cannot be simply ordered according to the intensity of light emission at a given temperature. The chemiluminescence-time patterns are related with the rate of sample oxidation, but they may differ from one to the next polymer. 

KEY TERMS amorphous crystalline diffraction hydrate solid emulsion... 

Figure 5.3. Effects of soil pH on the Zn amount bound to the Fe oxide fraction (amorphous/crystalline Fe oxide and overall Fe oxide bound fractions) in soils from China with pH 3.73-8.1 and 0-14.7% CaC03 (after Han et al., 1995. Reprinted from Geoderma, 66, Han F.X., Hu A.T., Qi H.Y., Transformation and distribution of forms of zinc in acid, neutral and calcareous soils of China, p 128, Copyright (1995), with permission from Elsevier)...

Oxygen diffuses inside the amorphous phase of amorphous crystalline polymers. The diffusion coefficient can be expressed for such polymers in the form [68]... 

A decrease in the coefficient a with an increase in temperature as a result of the intensification of the molecular mobility in the polymer matrix with the increase in temperature. The increase in temperature decreases the energetic barrier Eor. In the amorphous-crystalline polymers all these processes occur in the amorphous phase of the polymer where reactants are dissolved. 

Structure as deposited Crystalline Crystalline/ amorphous Crystalline/ amorphous Amorphous Microcrystalline/ amorphous Mcirocrystalline/ amorphous Cross-linked... 

Polyethylene is an organic polymer with an amorphous crystalline structure, formed by the polymerization of ethylene gas. A low-density polyethylene with a processing temperature of 130 to 150°C has been evaluated in bench-scale and full-scale tests as a final waste form for evaporator concentrates, sludges, blowdown solutions, incinerator ash, and ion exchange resins. 

Al-rich minerals Alunite Amorphous Crystalline Alunogen Basaluminite Amorphous Crystalline Halotrichite Pickcringite... 

A polymer may be amorphous, crystalline, or a combination of both. Many polymers actually have both crystalline and amorphous regions, i.e., a semicrystalline polymer. The Tg is a transition related to the motion in the amorphous regions of the polymer [3,8,9], Below the Tg, an amorphous polymer can be said... 

---