Poly absorption

Poly(lactide-coglycolide). Mixtures of lactide and glycolide monomers have been copolymerised in an effort to extend the range of polymer properties and rates of in vivo absorption. Poly(lactide- (9-glycolide) polymers undergo a simple hydrolysis degradation mechanism, which is sensitive to both pH and the presence of ensymes (32). 

The windows of the absorption cell are made from polymer material such as polyethylene, poly(ethylene terephthalate Terylene ) or polystyrene. 

Fig. 4. Chemistry of poly(vinyl cinnamate) negative-acting resist. Initial light absorption by the photosensitizer is followed by energy transfer to produce a pendant cinnamate group in a triplet electronic state. This combines with a second cinnamate on another polymer chain, forming a polymer—polymer...

Acrolein is highly toxic by skin absorption. Brief contact may result in the absorption of harmful and possibly fatal amounts of material. Skin contact causes severe local irritation and chemical bums. Poly(vinyl chloride) coated protective gloves should be used (99). 

Polyimide. Polyimide is a biaxiaHy oriented high performance film that is tough, flexible, and temperature- and combustion-resistant. Its room temperature properties compare to poly(ethylene terephthalate), but it retains these good characteristics at temperatures above 400°C. Its electrical resistance is good and it is dimensionally stable. The principal detriment is fairly high moisture absorbance. The main uses are for electrical insulation, particularly where high temperatures are prevalent or ionizing radiation is a problem. The films may be coated to reduce water absorption and enhance... 

Decafluorobiphenyl [434-90-2] C F C F (mol wt, 334.1 mp, 68°C bp, 206°C), can be prepared by I Jllmann coupling of bromo- [344-04-7] chloro- [344-07-0] or iodopentafluorobenzene [827-15-6] with copper. This product shows good thermal stabiHty decafluorobiphenyl was recovered unchanged after 1 h below 575°C (270). Decafluorobiphenyl-based derivatives exhibit greater oxidative stabiHty than similar hydrocarbon compounds (271). Therm ally stable poly(fluorinated aryl ether) oligomers prepared from decafluorobiphenyl and bisphenols show low dielectric constant and moisture absorption which are attractive for electronic appHcations (272). 

A solubihty parameter of 24.5-24.7 MPa / [12.0-12.1 (cal/cm ) ] has been calculated for PVF using room temperature swelling data (69). The polymer lost solvent to evaporation more rapidly than free solvent alone when exposed to air. This was ascribed to reestabUshment of favorable dipole—dipole interactions within the polymer. Infrared spectral shifts for poly(methyl methacrylate) in PVF have been interpreted as evidence of favorable acid—base interactions involving the H from CHF units (70). This is consistent with the greater absorption of pyridine than methyl acetate despite a closer solubihty parameter match with methyl acetate. 

Poly(methyl methacrylate). PMMA offers distinct advantages over BPA-PC with respect to significandy lower birefringence, higher modulus, and lower costs, but has not been successhil as a material for audio CDs and CD-ROM as well as a substrate material for WORM and EOD disks because of its high water absorption (which makes it prone to warp) and its unsuitabiUty for metallising, and less so because of its low resistance to... 

Fig. 26. Qualitative compatison of substrate materials for optical disks (187) An = birefringence IS = impact strength BM = bending modulus HDT = heat distortion temperature Met = metallizability WA = water absorption Proc = processibility. The materials are bisphenol A—polycarbonate (BPA-PC), copolymer (20 80) of BPA-PC and trimethylcyclohexane—polycarbonate (TMC-PC), poly(methyl methacrylate) (PMMA), uv-curable cross-linked polymer (uv-DM), cycHc polyolefins (CPO), and, for comparison, glass.

The actual time required for poly-L-lactide implants to be completely absorbed is relatively long, and depends on polymer purity, processing conditions, implant site, and physical dimensions of the implant. For instance, 50—90 mg samples of radiolabeled poly-DL-lactide implanted in the abdominal walls of rats had an absorption time of 1.5 years with metaboHsm resulting primarily from respiratory excretion (24). In contrast, pure poly-L-lactide bone plates attached to sheep femora showed mechanical deterioration, but Httie evidence of significant mass loss even after four years (25). 

The absorption rate has been examined in vivo for a series of poly(ester—amides) having the following formula ... 

Sorbitan sesquioleate emulsions of petrolatum and wax are used as ointment vehicles in skin treatment. In topical appHcations, the inclusion of both sorbitan fatty esters and their poly(oxyethylene) derivatives modifies the rate of release and promotes the absorption of antibiotics, antiseptics, local anesthetics, vasoconstrictors, and other medications from suppositories, ointments, and lotions. Poly(oxyethylene(20)) sorbitan monooleate, also known as Polysorbate 80 (USP 23), has been used to promote absorption of ingested fats from the intestine (245). 

The nmr spectmm of PVAc iu carbon tetrachloride solution at 110°C shows absorptions at 4.86 5 (pentad) of the methine proton 1.78 5 (triad) of the methylene group and 1.98 5, 1.96 5, and 1.94 5, which are the resonances of the acetate methyls iu isotactic, heterotactic, and syndiotactic triads, respectively. Poly(vinyl acetate) produced by normal free-radical polymerization is completely atactic and noncrystalline. The nmr spectra of ethylene vinyl acetate copolymers have also been obtained (33). The ir spectra of the copolymers of vinyl acetate differ from that of the homopolymer depending on the identity of the comonomers and their proportion. 

Poly(vinyl acetate) chains are also stabilized as aqueous-soluble anionic species by complexation with a surfactant. The charge on the water-soluble species prevents their absorption into the particle (114). 

Plasticizers. Plasticizers are materials that soften and flexibilize inherently rigid, and even britde polymers. Organic esters are widely used as plasticizers in polymers (97,98). These esters include the benzoats, phthalates, terephthalates, and trimeUitates, and aUphatic dibasic acid esters. Eor example, triethylene glycol bis(2-ethylbutyrate) [95-08-9] is a plasticizer for poly(vinyl butyral) [63148-65-2] which is used in laminated safety glass (see Vinyl POLYMERS, poly(vinyl acetals)). Di(2-ethyUiexyl)phthalate [117-81-7] (DOP) is a preeminent plasticizer. Variation of acid and/or alcohol component(s) modifies the efficacy of the resultant ester as a plasticizer. In phthalate plasticizers, molecular sizes of the alcohol moiety can be varied from methyl to tridecyl to control permanence, compatibiUty, and efficiency branched (eg, 2-ethylhexyl, isodecyl) for rapid absorption and fusion linear (C6—Cll) for low temperature flexibiUty and low volatility and aromatic (benzyl) for solvating. Terephthalates are recognized for their migration resistance, and trimeUitates for their low volatility in plasticizer appHcations. 

Although poly(vinyl fluoride) resembles PVC in its low water absorption, resistance to hydrolysis, insolubility in common solvents at room temperature and a tendency to split off hydrogen halides at elevated temperatures, it has a much greater tendency to crystallise. This is because the fluorine atom (c.f. the chlorine atom) is sufficiently small to allow molecules to pack in the same way as polythene. 

---