Viscoelasticity normal stress

In the foregoing derivations we neglected the inertia term in eq. 5.4.1. We saw with concentric cylinders that inertia causes a depression around the inner cylinder rather than the climb due to viscoelastic normal stresses (Figure 5.3.3). In cone and plate... [Pg.209]

Trends in interlayer adhesion in coextruded structures have been correlated to the nonlinear viscoelastic normal stresses in the interface vicinity using an ordering parameter called Viscosity Normalized Nonlinearity Ratio . Larger deviation of this parameter from a value of 1.0 (large disparities in melt extensional configuration across the interface) corresponded to poorer observed peel strength. This parameter is of particular importance in the region where the melt layers come into contact for the first time, in scenarios where polymer relaxation times are of a similar order as the flow timescales. [Pg.2861]

Figure 6 Nonlinear viscoelastic normal stress ratio parameter for the different coextruded formulations... Figure 6 Nonlinear viscoelastic normal stress ratio parameter for the different coextruded formulations...
Material parameters defined by Equations (1.11) and (1.12) arise from anisotropy (i.e. direction dependency) of the microstructure of long-chain polymers subjected to liigh shear deformations. Generalized Newtonian constitutive equations cannot predict any normal stress acting along the direction perpendicular to the shearing surface in a viscometric flow. Thus the primary and secondary normal stress coefficients are only used in conjunction with viscoelastic constitutive models. [Pg.6]

The practical and computational complications encountered in obtaining solutions for the described differential or integral viscoelastic equations sometimes justifies using a heuristic approach based on an equation proposed by Criminale, Ericksen and Filbey (1958) to model polymer flows. Similar to the generalized Newtonian approach, under steady-state viscometric flow conditions components of the extra stress in the (CEF) model are given a.s explicit relationships in terms of the components of the rate of deformation tensor. However, in the (CEF) model stress components are corrected to take into account the influence of normal stresses in non-Newtonian flow behaviour. For example, in a two-dimensional planar coordinate system the components of extra stress in the (CEF) model are written as... [Pg.14]

In generalized Newtonian fluids, before derivation of the final set of the working equations, the extra stress in the expanded equations should be replaced using the components of the rate of strain tensor (note that the viscosity should also be normalized as fj = rj/p). In contrast, in the modelling of viscoelastic fluids, stress components are found at a separate step through the solution of a constitutive equation. This allows the development of a robust Taylor Galerkin/ U-V-P scheme on the basis of the described procedure in which the stress components are all found at time level n. The final working equation of this scheme can be expressed as... [Pg.136]

Solution of the flow equations has been based on the application of the implicit 0 time-stepping/continuous penalty scheme (Chapter 4, Section 5) at a separate step from the constitutive equation. The constitutive model used in this example has been the Phan-Thien/Tanner equation for viscoelastic fluids given as Equation (1.27) in Chapter 1. Details of the finite element solution of this equation are published elsewhere and not repeated here (Hou and Nassehi, 2001). The predicted normal stress profiles along the line AB (see Figure 5.12) at five successive time steps are. shown in Figure 5.13. The predicted pattern is expected to be repeated throughout the entire domain. [Pg.157]

These normal stresses are more pronounced for polymers with a very broad molecular weight distribution. Viscosities and viscoelastic behavior decrease with increasing temperature. In some cases a marked viscosity decrease with time is observed in solutions stored at constant temperature and 2ero shear. The decrease may be due to changes in polymer conformation. The rheological behavior of pure polyacrylamides over wide concentration ranges has been reviewed (5). [Pg.140]

Polyolefin melts have a high degree of viscoelastic memory or elasticity. First normal stress differences of polyolefins, a rheological measure of melt elasticity, are shown in Figure 9 (30). At a fixed molecular weight and shear rate, the first normal stress difference increases as MJM increases. The high shear rate obtained in fine capillaries, typically on the order of 10 , coupled with the viscoelastic memory, causes the filament to swell (die swell or... [Pg.317]

For some materials the linear constitutive relation of Newtonian fluids is not accurate. Either stress depends on strain in a more complex way, or variables other than the instantaneous rate of strain must be taken into account. Such fluids are known collectively as non-Newtonian. Many different types of behavior have been observed, ranging from fluids for which the viscosity in the Navier-Stokes equation is a simple function of the shear rate to the so-called viscoelastic fluids, for which the constitutive equation is so different that the normal stresses can cause the fluid to flow in a manner opposite to that predicted for a Newtonian fluid. [Pg.89]

Many industrially important fluids cannot be described in simple terms. Viscoelastic fluids are prominent offenders. These fluids exhibit memory, flowing when subjected to a stress, but recovering part of their deformation when the stress is removed. Polymer melts and flour dough are typical examples. Both the shear stresses and the normal stresses depend on the history of the fluid. Even the simplest constitutive equations are complex, as exemplified by the Oldroyd expression for shear stress at low shear rates ... [Pg.96]

Normal Stress (Weissenberg Effect). Many viscoelastic fluids flow in a direction normal (perpendicular) to the direction of shear stress in steady-state shear (21,90). Examples of the effect include flour dough climbing up a beater, polymer solutions climbing up the inner cylinder in a concentric cylinder viscometer, and paints forcing apart the cone and plate of a cone—plate viscometer. The normal stress effect has been put to practical use in certain screwless extmders designed in a cone—plate or plate—plate configuration, where the polymer enters at the periphery and exits at the axis. [Pg.178]

The Weissenberg Rheogoniometer (49) is a complex dynamic viscometer that can measure elastic behavior as well as viscosity. It was the first rheometer designed to measure both shear and normal stresses and can be used for complete characteri2ation of viscoelastic materials. Its capabiUties include measurement of steady-state rotational shear within a viscosity range of 10 — mPa-s at shear rates of, of normal forces (elastic... [Pg.189]

Rheometric Scientific markets several devices designed for characterizing viscoelastic fluids. These instmments measure the response of a Hquid to sinusoidal oscillatory motion to determine dynamic viscosity as well as storage and loss moduH. The Rheometric Scientific line includes a fluids spectrometer (RFS-II), a dynamic spectrometer (RDS-7700 series II), and a mechanical spectrometer (RMS-800). The fluids spectrometer is designed for fairly low viscosity materials. The dynamic spectrometer can be used to test soHds, melts, and Hquids at frequencies from 10 to 500 rad/s and as a function of strain ampHtude and temperature. It is a stripped down version of the extremely versatile mechanical spectrometer, which is both a dynamic viscometer and a dynamic mechanical testing device. The RMS-800 can carry out measurements under rotational shear, oscillatory shear, torsional motion, and tension compression, as well as normal stress measurements. Step strain, creep, and creep recovery modes are also available. It is used on a wide range of materials, including adhesives, pastes, mbber, and plastics. [Pg.202]

When the magnitude of deformation is not too great, viscoelastic behavior of plastics is often observed to be linear, i.e., the elastic part of the response is Hookean and the viscous part is Newtonian. Hookean response relates to the modulus of elasticity where the ratio of normal stress to corresponding strain occurs below the proportional limit of the material where it follows Hooke s law. Newtonian response is where the stress-strain curve is a straight line. [Pg.42]

Viscoelastic fluids are thus capable of exerting normal stresses. Because most materials, under appropriate circumstances, show simultaneously solid-like and fluid-like behaviours in varying proportions, the notion of an ideal elastic solid or of a purely viscous fluid represents the commonly encountered limiting condition. For instance, the viscosity of ice and the elasticity of water may both pass unnoticed The response of a material may also depend upon the type of deformation to which it is subjected. A material may behave like a highly elastic solid in one flow situation, and like a viscous fluid in another. [Pg.116]

Dynamic similarity occurs in two geometrically similar units of different sizes if all corresponding forces at counterpart locations have a constant ratio. It is necessary here lo distinguish between the various types of force inertial, gravitational, viscous, surface tension and other forms, such as normal stresses in the case of viscoelastic non-Newtonian liquids. Some or all of these forms may be significant in a mixing vessel. Considering... [Pg.280]

Non-linear viscoelastic flow phenomena are one of the most characteristic features of polymeric liquids. A matter of very emphasised interest is the first normal stress difference. It is a well-accepted fact that the first normal stress difference Nj is similar to G, a measure of the amount of energy which can be stored reversibly in a viscoelastic fluid, whereas t12 is considered as the portion that is dissipated as viscous flow [49-51]. For concentrated solutions Lodge s theory [52] of an elastic network also predicts normal stresses, which should be associated with the entanglement density. [Pg.10]

The coordinates (x, y, z) define the (velocity, gradient, vorticity) axes, respectively. For non-Newtonian viscoelastic liquids, such flow results not only in shear stress, but in anisotropic normal stresses, describable by the first and second normal stress differences (oxx-Oyy) and (o - ozz). The shear-rate dependent viscosity and normal stress coefficients are then [1]... [Pg.188]

As a result, we find for sols that the divergence of the above zero shear viscosity rj0 and of two other linear viscoelastic material functions, first normal stress coefficient and equilibrium compliance 7°, depends on the divergence... [Pg.177]

Here we describe the strain history with the Finger strain tensor C 1(t t ) as proposed by Lodge [55] in his rubber-like liquid theory. This equation was found to describe the stress in deforming polymer melts as long as the strains are small (second strain invariant below about 3 [56] ). The permanent contribution GcC 1 (r t0) has to be added for a linear viscoelastic solid only. C 1(t t0) is the strain between the stress free state t0 and the instantaneous state t. Other strain measures or a combination of strain tensors, as discussed in detail by Larson [57], might also be appropriate and will be considered in future studies. A combination of Finger C 1(t t ) and Cauchy C(t /. ) strain tensors is known to express the finite second normal stress difference in shear, for instance. [Pg.189]

We can also calculate other viscoelastic properties in the limit of low shear rate (linear viscoelastic limit) near the LST. The above simple spectrum can be integrated to obtain the zero shear viscosity 0, the first normal stress coefficient if/1 at vanishing shear rate, and the equilibrium compliance J... [Pg.194]

In order to simplify the discussion and keep the derivation of the formulae tractable, a fibre with a single orientation angle is considered. In a creep experiment the tensile deformation of the fibre is composed of an immediate elastic and a time-dependent elastic extension of the chain by the normal stress ocos20(f), represented by the first term in the equation, and of an immediate elastic, viscoelastic and plastic shear deformation of the domain by the shear stress, r =osin0(f)cos0(f), represented by the second term in Eq. 106. [Pg.83]

When a viscoelastic liquid flows through a tube, the normal stress differences cause the liquid to be under an axial tension while a normal... [Pg.131]

Another well-known phenomenon is the Weissenberg effect, which occurs when a long vertical rod is rotated in a viscoelastic liquid. Again, the shearing generates a tension along the streamlines, which are circles centred on the axis of the rod. The only way in which the liquid can respond is to flow inwards and it therefore climbs up the rod until the hydrostatic head balances the force due to the normal stresses. [Pg.132]

A less well known effect occurs in open channel flow of a viscoelastic liquid, when the normal stress differences cause the free surface to bow upwards in the centre [Tanner (1985)]. [Pg.132]

The Weissenbeig Rheogoniometer (49) is a complex dynamic viscometer that can measure elastic behavior as well as viscosity. It was the first rheometer designed to measure both shear and normal stresses and can be used for complete characterization of viscoelastic materials. Its capabilities include measurement of steady-state rotational shear within a viscosity range of 10-1 —13 mPa-s at shear rates of 10-4 — 104 s-1, of normal forces (elastic effect) exhibited by the material being sheared, and of an oscillatory shear range of 5 x 10-6 to 50 Hz, from which the elastic modulus and dynamic viscosity can be determined. A unique feature is its ability to superimpose oscillation on steady shear to provide dynamic measurements under flow conditions all measurements can be made over a wide range of temperatures (—50 to 400°C). [Pg.189]

Another often used representation of the viscoelastic flow behavior utilizes normal stress coefficients P/ = Ni/y. Figure 10 depicts flow curves of a family of PAA/water solutions differing in concentrations and therefore in their viscosities. Normalized by the zero-shear viscosity fiQ and by a constant shear rate /q shear stress value of to= 1 N/m they produce master curves for viscosity and the normal stress coefficient. The preparation... [Pg.28]

Elastic behavior of liquids is characterized mainly by the ratio of first differences in normal stress, Ni, to the shear stress, t. This ratio, the Weissenberg number Wi = Nih, is usually represented as a function of the rate of shear y. Figure 7 depicts flow curves of some viscoelastic fluids, and Figure 8 presents a dimensionless standardized material function of these fluids. It again verifies that they behave similarly with respect to viscoelastic behavior under shear stress. [Pg.27]


See other pages where Viscoelasticity normal stress is mentioned: [Pg.107]    [Pg.388]    [Pg.107]    [Pg.388]    [Pg.9]    [Pg.10]    [Pg.96]    [Pg.172]    [Pg.178]    [Pg.631]    [Pg.587]    [Pg.93]    [Pg.114]    [Pg.118]    [Pg.35]    [Pg.383]    [Pg.414]    [Pg.131]    [Pg.172]    [Pg.178]    [Pg.100]   
See also in sourсe #XX -- [ Pg.2 , Pg.961 ]




SEARCH



Normal stress

Viscoelastic behaviour normal stresses

Viscoelastic stress

© 2024 chempedia.info