Vinyl-type monomers, block

If (P ) is terminated by a chain transfer to a solvent or a monomer, a graft copolymer is formed, or, if the termination is from a combination, a crosslinked network polymer is formed. If the pre-existing polymer (B) contains an end group that itself is photosensitive (or can produce a radical by interacting with photoinitiator) and in the presence of a vinyl monomer (A), block copolymer of type AB can be produced if the photosensitive group is on one end of the polymeric chain. Type ABA block copolymer can be produced if the polymer chain (B) contains a photosensitive group on both ends. 

To obtain a high molecular weight block or random copolymer of the oxonium ion type monomer and carbonium ion type monomer, experimental conditions must be such that termination or transfer reactions are minimized. The living nature of the cationic polymerization of THF (7) is well established, but it has been difficult to obtain a high polymer of styrene or DOL by cationic mechanism. In this paper we demonstrate the living nature of the polymerization of DOL and the high polymer of St-DOL copolymer. Using this technique, we were able to obtain a block copolymer of vinyl monomer and cyclic monomer. 

This technique allows formation of many different types of block copolymers [437]. Lithium metal can be used to initiate polymerizations in solvents of varying polarity. Monomers, like styrene, a-methylstyrene, methyl methacrylate, butyl methacrylate, 2-vinylp3Tidine, 4-vinyl pyridine, acrylonitrile, and methyl acrylate, can be used. The mechanism of initiation depends upon formation of ion-radicals through reactions of lithium with the double bonds ... 

NR, styrene-butadiene mbber (SBR), polybutadiene rubber, nitrile mbber, acrylic copolymer, ethylene-vinyl acetate (EVA) copolymer, and A-B-A type block copolymer with conjugated dienes have been used to prepare pressure-sensitive adhesives by EB radiation [116-126]. It is not necessary to heat up the sample to join the elastomeric joints. This has only been possible due to cross-linking procedure by EB irradiation [127]. Polyfunctional acrylates, tackifier resin, and other additives have also been used to improve adhesive properties. Sasaki et al. [128] have studied the EB radiation-curable pressure-sensitive adhesives from dimer acid-based polyester urethane diacrylate with various methacrylate monomers. Acrylamide has been polymerized in the intercalation space of montmorillonite using an EB. The polymerization condition has been studied using a statistical method. The product shows a good water adsorption and retention capacity [129]. 

The copolymerization of multimonomers with vinyl monomers such as acrylic acid, styrene, or acrylonitrile results in semi-ladder copolymers soluble in many common sol-vents. Such products consist of ladder-type blocks created from multimonomer molecules and blocks of repeated units formed from vinyl monomer, both connected with branching points and fastened together by fragments of the molecule with ladder structure. Semi-ladder copolymer (multimethacrylate-acrylic acid, partially crosslinked) has the following structure ... 

A similar method of hydrolysis was described for poly( vinyl alcohol) used as a template. In this case, T was -CH2-CH- and, after hydrolysis, poly(vinyl alcohol) and polyacrylic or polymethacrylic acid were obtained. The hydrolyzed product gives the color reaction with I2 in the presence of H3BO3 - specific to poly(vinyl alcohol). The second product of hydrolysis, after esterification by diazomethane, was identified as polyfmethyl methacrylate) by NMR and IR spectrometry. Hydrolysis was also applied in the case of ladder-type polymers obtained by polymerization of mutliallyl monomers. The polymerization should result in polymer consisting, at least partly, ladder-type blocks ... 

Homopolymers of polybutadiene can consist of three basic isomeric forms (czs-1,4, trans-1,4, and 1,2 vinyl), and these can be present in different sequential order. Copolymers may obtain a variety of co-monomers, such as styrene, acrylonitrile, etc. Depending on their distribution in the chain, random copolymers or block copolymers of different types and perfection can be produced. There are many synthetic elastomers based on butadiene available commercially. 

Three arm amphiphilic star block copolymers of IBVE and 2-hydroxyethyl vinyl ether (HOVE) were prepared using the trifunctional initiator 8 with sequential cationic polymerization of two hydrophobic monomers, IBVE and AcOVE. Subsequent hydrolysis of the acetates led to the hydrophilic poly(HOVE) segments [38]. Two types of stars were prepared depending on which monomer was polymerized first three arm star poly(IBVE-h-HOVE), with the hydrophobic part inside and three arm star poly(HOVE-h-IBVE), with the hydrophobic part outside. When IBVE was polymerized first, the experimental conditions were the same as described in Sect. 2.2.1. After reaching quantitative monomer conversion, AcOVE was added and temperature was raised from 0 to 40 °C to accelerate the reaction since this monomer is less reactive than IBVE. When starting with AcOVE as a first block, both polymerizations were carried out at 40 °C. SEC analysis showed that MWDs were narrow for the two steps whatever the se-... 

---