Short fiber-rubber composites fibers used

Proper reinforcement of rubber matrix using hllers can be achieved only if there exists adequate adhesion between the hller and the mbber. Rubber-mbber adhesion and rubber-hller adhesion both without and with adhesion promoters have been studied extensively [125-127]. Fiber-matrix adhesion in short fiber-rubber composites is always a field of extensive research. If the fibers are not bonded properly with the rubber matrix, fibers will shde past each other under tension deforming the matrix, thereby reducing the strength properties. In the case of short fiber-reinforced rubber composites, loads are not directly applied to the fibers, but are apphed to the matrix. To obtain a high-performance composite, the load must be effectively transferred to the fibers, which is possible only when the fiber-matrix interphase is sufficiently strong. In addition, the adhesion between the fiber and the matrix should be such that the failure occurs in the matrix rather than at the interphase [92]. 

Fluoroelastomers Novikova et al. [32] reported unproved physico-mechanical properties of fluoro mbbers by reinforcement with chopped polyamide fibers. Other fiber reinforcements are covered by Grinblat et al. [33]. Watson and Francis [34] described the use of aramid (Kevlar) as short fiber reinforcement for vulcanized fluoroelastomer along with polychloroprene mbber and a co-polyester TPE in terms of improvement in the wear properties of the composites. Rubber diaphragms, made up of fluorosilicone mbbers, can be reinforced using aramid fiber in order to impart better mechanical properties to the composite, though surface modification of the fiber is needed to improve the adhesion between fluorosUicone mbber and the fiber [35]. Bhattacharya et al. [36] studied the crack growth resistance of fluoroelastomer vulcanizates filled with Kevlar fiber. 

The reinforcement of rubbers using nylon, rayon, vinyl, and polyester fibers was reported by various authors [10,58,73-75]. Because of the design flexibility and suitable end-use applications, high-performance fibers such as glass, carbon, and aramid also find extensive applications in short fiber-reinforced mbbers. A brief description of some of the major high-performance fibers commonly used in short fiber-rubber composites is given below ... 

There is a wide variety of materials which are foreign to the body and which are used in contact with body fluids. These materials are called biomaterials. They include polymers (fibers, rubbers, molded plastics, emulsions, coatings, fluids, etc.), metals, ceramics, carbons, reconstituted or specially treated natural tissues, and composites made from various combinations of such materials (Table 1). Some are needed only for short-term applications while others are, hopefully, useful for the lifetime of the individual. Apphcations include devices or implants for diagnosis or therapy. 

Liquid rubbers In order to improve the flexibihty of short glass fiber-reinforced epoxy composites, Kaynak et al. [53] modified the epoxy resin matrix with hydroxyl-terminated polybutadiene (HTPB) liquid mbber. A silane coupling agent was also used to improve the interfacial adhesion between glass fibers and epoxy matrix. However, Humpidge et al. [54] reported some unique processing problems for the resulting pasty mixmres when short textile fibers were incorporated in a hquid mbber medium. 

---