Polyolefin polymer specific gravity

Aluminium hydroxide has a Moh hardness of about 3 and a specific gravity of 2.4. It decomposes endothermically with the release of water at about 200 °C and this makes it a very useful flame retardant filler, this being the principal reason for its use in polymers. The decomposition temperature is in fact too low for many thermoplastics applications, but it is widely used in low smoke P VC applications and finds some use in polyolefins. For these applications low aspect ratio particles with a size of about 1 micron and a specific surface area of 4-10 m g are preferred. The decomposition pathway can be diverted through the mono-hydrate by the application of pressure, and this may reduce the flame retardant effect [97]. This effect can be observed with the larger sized particles. Although it is chemically the hydroxide, it has for many years been known as alumina trihydrate and by the acronym ATH. 

Zinc oxide (ZnO) is widely used as an active filler in rubber and as a weatherability improver in polyolefins and polyesters. Titanium dioxide (TiOj) is widely used as a white pigment and as a weatherability improver in many polymers. Ground barites (BaS04) yield x-ray-opaque plastics with controlled densities. The addition of finely divided calcined alumina or silicon carbide produces abrasive composites. Zirconia, zirconium silicate, and iron oxide, which have specific gravities greater than 4.5, are used to produce plastics with controlled high densities. 

Alcryn (Advanced Polymer Alloys Division of Ferro Corporation) is an example of a melt-processable rubber. These are partially cross-linked halogenated polyolefin MPR blends. The specific gravity ranges from 1.08 to 1.35. 

This polyolefin family polymer has a specific gravity of 0.88 and floats on water. It burns with a blue flame with a yellow tip and gives off an acrid odor similar to diesel fumes. The material is soluble in hot toluene. Polypropylene is positively identified by an infrared spectrometer. 

---