Polymerization reactions, advantages

Calcium Chelates (Salicylates). Several successhil dental cements which use the formation of a calcium chelate system (96) were developed based on the reaction of calcium hydroxide [1305-62-0] and various phenohc esters of sahcyhc acid [69-72-7]. The calcium sahcylate [824-35-1] system offers certain advantages over the more widely used zinc oxide—eugenol system. These products are completely bland, antibacterial (97), facihtate the formation of reparative dentin, and do not retard the free-radical polymerization reaction of acryhc monomer systems. The principal deficiencies of this type of cement are its relatively high solubihty, relatively low strength, and low modulus. Less soluble and higher strength calcium-based cements based on dimer and trimer acid have been reported (82). 

The ionic liquid process has a number of advantages over traditional cationic polymerization processes such as the Cosden process, which employs a liquid-phase aluminium(III) chloride catalyst to polymerize butene feedstocks [30]. The separation and removal of the product from the ionic liquid phase as the reaction proceeds allows the polymer to be obtained simply and in a highly pure state. Indeed, the polymer contains so little of the ionic liquid that an aqueous wash step can be dispensed with. This separation also means that further reaction (e.g., isomerization) of the polymer s unsaturated ot-terminus is minimized. In addition to the ease of isolation of the desired product, the ionic liquid is not destroyed by any aqueous washing procedure and so can be reused in subsequent polymerization reactions, resulting in a reduction of operating costs. The ionic liquid technology does not require massive capital investment and is reported to be easily retrofitted to existing Cosden process plants. 

Radical polymerization is the most useful method for a large-scale preparation of various kinds of vinyl polymers. More than 70 % of vinyl polymers (i. e. more than 50 % of all plastics) are produced by the radical polymerization process industrially, because this method has a large number of advantages arising from the characteristics of intermediate free-radicals for vinyl polymer synthesis beyond ionic and coordination polymerizations, e.g., high polymerization and copolymerization reactivities of many varieties of vinyl monomers, especially of the monomers with polar and unprotected functional groups, a simple procedure for polymerizations, excellent reproducibility of the polymerization reaction due to tolerance to impurities, facile prediction of the polymerization reactions from the accumulated data of the elementary reaction mechanisms and of the monomer structure-reactivity relationships, utilization of water as a reaction medium, and so on. 

Supercritical fluids have also been used purely as the solvent for polymerization reactions. Supercritical fluids have many advantages over other solvents for both the synthesis and processing of materials (see Chapter 6), and there are a number of factors that make scCCH a desirable solvent for carrying out polymerization reactions. As well as being cheap, nontoxic and nonflammable, separation of the solvent from the product is achieved simply by depressurization. This eliminates the energy-intensive drying steps that are normally required after the reaction. Carbon dioxide is also chemically relatively inert and hence can be used for a wide variety of reactions. For example, CO2 is inert towards free radicals and this can be important in polymerization reactions since there is then no chain transfer to the solvent. This means that solvent incorporation into the polymer does not take place, giving a purer material. 

With appropriate precautions, condensation and addition polymerization reactions can be carried out in the same apparatus as customarily used for organic preparative work (see Sects. 4.1 and 4.2). In order to obtain high molecular weights by polycondensation in solution, a special circulation apparatus can be advantageously used with advantage (Fig. 2.4). 

S Gas-Phase Polymerization. Not all polymerization reactions are carried out in the liquid phase. Polyethylene, for example, can be polymerized not only in solution as discussed in Section 3.3.2.2, but also through gas-phase polymerization (see Figure 3.28). Significant economic advantage is gained by eliminating costly solvent and catalyst recovery equipment. A fluidized bed reactor is used, into which purified... 

---