Polymer melting time-dependent processes during

Polymorphism. Many crystalline polyolefins, particularly polymers of a-olefins with linear alkyl groups, can exist in several polymorphic modifications. The type of polymorph depends on crystallisa tion conditions. Isotactic PB can exist in five crystal forms form I (twinned hexagonal), form II (tetragonal), form III (orthorhombic), form P (untwinned hexagonal), and form IP (37—39). The crystal stmctures and thermal parameters of the first three forms are given in Table 3. Form II is formed when a PB resin crystallises from the melt. Over time, it is spontaneously transformed into the thermodynamically stable form I at room temperature, the transition takes about one week to complete. Forms P, IP, and III of PB are rare they can be formed when the polymer crystallises from solution at low temperature or under pressure (38). Syndiotactic PB exists in two crystalline forms, I and II (35). Form I comes into shape during crystallisation from the melt (very slow process) and form II is produced by stretching form-1 crystalline specimens (35). 

---