Poly(vinyhdene chloride) (PVDC) film has exceUent barrier properties, among the best of the common films (see Barrier polymers). It is formulated and processed into a flexible film with cling and tacky properties that make it a useful wrap for leftovers and other household uses. As a component in coatings or laminates it provides barrier properties to other film stmctures. The vinyUdene chloride is copolymerized with vinyl chloride, alkyl acrylates, and acrylonitrile to get the optimum processibUity and end use properties (see Vinylidene chloride monomer and polymers). 

Poly(glycolide-co trimethylene carbonate). Another successful approach to obtaining an absorbable polymer capable of producing flexible monofilaments has involved finding a new type of monomer for copolymerization with glycoHde (42). Trimethylene carbonate polymerized with glycoHde is shown below ... 

Although they lack commercial importance, many other poly(vinyl acetal)s have been synthesized. These include acetals made from vinyl acetate copolymerized with ethylene (43—46), propjiene (47), isobutjiene (47), acrylonitrile (48), acrolein (49), acrylates (50,47), aHyl ether (51), divinyl ether (52), maleates (53,54), vinyl chloride (55), diaHyl phthalate (56), and starch (graft copolymer) (47). 

Liquid trichloroethylene has been polymerized by irradiation with Co y-rays or 20-keV x-rays (9). Trichloroethylene has a chain-transfer constant of <1 when copolymerized with vinyl chloride (10) and is used extensively to control the molecular weight of poly(vinyl chloride) polymer. 

Recently, the pyrazole group containing bisphenols have been synthesized from activated aromatic dihalides and 3,5-bis (4-hydroxy phenyl)-4-phenyl pyrazole or 3,5-bis(4-hydroxy phenyl)-1,4-diphenyl pyrazole. A novel synthesis of imido aryl containing bisphenols has been reported [32]. N-substituted l,4-bis(4-hydroxy phenyl)-2,3-naphthalimides were prepared from phenolphthalein and copolymerized with aromatic sulfone or ketone difluorides to obtain the poly(imidoaryl ether) sulfones/ ketones. 

Styrene monomer was also copolymerized with a series of functional monomers by using a single-step dispersion copolymerization procedure carried out in ethanol as the dispersion medium by using azobisizobu-tyronitrile and polyvinylpyrollidone as the initiator and the stabilizer, respectively [84]. The comonomers were methyl methacrylate, hydroxyethyl acrylate, metha-crylic acid, acrylamide, allyltrietoxyl silane, vinyl poly-dimethylsiloxane, vinylsilacrown, and dimethylamino-... 

Apart from poly(ethylene glycol), other hydroxyl-terminated polymers and low-molecular weight compounds were condensed with ACPC. An interesting example is the reaction of ACPC with preformed poly(bu-tadiene) possessing terminal OH groups [26]. The reaction was carried out in chloroform solution and (CH3CH2)3N was used as a catalyst. MAIs based on butadiene thus obtained were used for the thermally induced block copolymerization with styrene [26] and dimethyl itaconate [27]. 

Polyaddition reactions based on isocyanate-terminated poly(ethylene glycol)s and subsequent block copolymerization with styrene monomer were utilized for the impregnation of wood [54]. Hazer [55] prepared block copolymers containing poly(ethylene adipate) and po-ly(peroxy carbamate) by an addition of the respective isocyanate-terminated prepolymers to polyazoesters. By both bulk and solution polymerization and subsequent thermal polymerization in the presence of a vinyl monomer, multiblock copolymers could be formed. 

These compds may be modified by monocar-boxy lie acids or poly hydroxy alcohols. This definition includes the polycarbonates (qv), which are a well-defined segment of the general class of polyesters. Unsaturated polyesters, which are produced when any of the reactants contain non-aromatic unsaturation, can be cross-linked or copolymerized with an un-saturated copolymerizable monomer. The formulas and properties of the class polyester are as varied and extensive as the reactants themselves. For specific information on the various sub-classes and sub-sub classes, the following refs should be consulted 9, 10, II, 16a, 17,18,... 

PAs have also been copolymerized with other polymer systems and, in particular", with polyesters and poly ethers. In the copoly esteramides the crystallinity is decreased by copolymerization, as the crystalline structure of the amide unit is very different from the ester unit. However, alternating polyesteramides behave as homopolymers with a glass ttansition temperature and a melting temperature intermediate to the polyester and the PA polymer (Figs. 3.10 and 3.11).23,24 Polyesters, such as PBT and PET, modified with a small amount of diamide are also copolymers that have a high order.24,73... 

The synthesis of PDMS macromonomers with vinyl silane end-groups and their free-radical copolymerization with vinyl acetate, leading to poly(vinyl acetate)-PDMS graft copolymers, was described 346). The copolymers produced were later hydrolyzed to obtain poly(vinyl alcohol)-PDMS graft copolymers. 

Vinyl chloride is used exclusively for the preparation of plastics, by homopolymerization to poly(vinyl chloride) (PVC) and by copolymerization with other vinyl (-CH2=CH-) compounds. 

The effect of hydrophobicity of the polymer on the permeability of poly(2-hydroxyethyl methacrylate (HEMA)-co-methacrylic acid (MAAc) hydrogels was studied [12], The hydrophobicity was controlled by copolymerization with butyl methacrylate (BMA). The dependence of permeability on pH increased as the hydrophobicity increased even though the rate of diffusion decreased. Cross-link density of the hydrogel also contributed to pH-dependent permeability. 

---