P-Phenylenes

White crystals, m.p. 114" C. Manufactured by reacting aniline with excess ethanoic acid or ethanoic anhydride. Chief use is in the manufacture of dye intermediates such as p-nitro-acetanilide, p-nitroaniline and p-phenylene-diamine, in the manufacture of rubber, and as a peroxide stabilizer. 

Steiner U B, Cased W R, Suter U W, Rehahn M and Rau I U 1994 Self-assembled layers of substituted poly(p-phenylene)s on gold and copper Langmuir 10 1164-70... 

The most noteworthy reaction of azo-compounds is their behaviour on reduction. Prolonged reduction first saturates the azo group, giving the hydrazo derivative (C NH-NH C), and then breaks the NH NH linkage, with the formation of two primary amine molecules. If method (1) has been employed to prepare the azo-compound, these two primary amines will therefore be respectively (a) the original amine from which the diazonium salt was prepared, and (6) the amino derivative of the amine or phenol with which the diazonium salt was coupled. For example, amino-azobenzene on complete reduction gives one equivalent of aniline, and one of p-phenylene diamine, NHaCeH NH benzene-azo-2-naphthoI similarly gives one equivalent of aniline and one of... 

Oxydi-p-phenylene-bis(4-phenyl and biphenyl-4-yl)thiazoles were also prepared in 62 to 63% yield (574). 

Compound 129, with R=Ph, p-MeCsH4, p-MeOC H, p-EtOC H, and 2-furyl, was obtained in 70 to 80% yield when p-phenylene bis-thiourea was heated with iodine and p-AcCaHjE, accxtrding to Method B (741). 

Polyheterocycles. Heterocychc monomers such as pyrrole and thiophene form hiUy conjugated polymers (4) with the potential for doped conductivity when polymerization occurs in the 2, 5 positions as shown in equation 6. The heterocycle monomers can be polymerized by an oxidative coupling mechanism, which can be initiated by either chemical or electrochemical means. Similar methods have been used to synthesize poly(p-phenylenes). 

Poly(arylene vinylenes). The use of the soluble precursor route has been successful in the case of poly(arylene vinylenes), both those containing ben2enoid and heteroaromatic species as the aryl groups. The simplest member of this family is poly(p-phenylene vinylene) [26009-24-5] (PPV). High molecular weight PPV is prepared via a soluble precursor route (99—105). The method involves the synthesis of the bis-sulfonium salt from /)-dichloromethylbenzene, followed by a sodium hydroxide elimination polymerization reaction at 0°C to produce an aqueous solution of a polyelectrolyte precursor polymer (11). This polyelectrolyte is then processed into films, foams, and fibers, and converted to PPV thermally (eq. 8). 

Eig. 2. Lattice distortions associated with the neutral, polaron, and bipolaron states in poly(p-phenylene). 

The polymers which have stimulated the greatest interest are the polyacetylenes, poly-p-phenylene, poly(p-phenylene sulphide), polypyrrole and poly-1,6-heptadiyne. The mechanisms by which they function are not fully understood, and the materials available to date are still inferior, in terms of conductivity, to most metal conductors. If, however, the differences in density are taken into account, the polymers become comparable with some of the moderately conductive metals. Unfortunately, most of these polymers also have other disadvantages such as improcessability, poor mechanical strength, instability of the doped materials, sensitivity to oxygen, poor storage stability leading to a loss in conductivity, and poor stability in the presence of electrolytes. Whilst many industrial companies have been active in their development (including Allied, BSASF, IBM and Rohm and Haas,) they have to date remained as developmental products. For a further discussion see Chapter 31. 

---