Oxide electrodes surface charge

Furthermore, metal oxide electrode surfaces are sites for acid/base equilibria. This situation leads to a strong solution pH dependence of the surface charges and, therefore, the potential drop in the double layer. In the absence of specific ion adsorption other than H" and OH", there will exist a particular solution pH for which the excess surface charge on the metal oxide is zero. This value of pH is called the zero point of charge (not to be confused with the pzc). If specific adsorption of ions other than H" and OH" occurs, then the solution pH at which no excess surface charge exists is called the isoelectronic point or the point of zero zeta potential. ... 

Electrode processes are a class of heterogeneous chemical reaction that involves the transfer of charge across the interface between a solid and an adjacent solution phase, either in equilibrium or under partial or total kinetic control. A simple type of electrode reaction involves electron transfer between an inert metal electrode and an ion or molecule in solution. Oxidation of an electroactive species corresponds to the transfer of electrons from the solution phase to the electrode (anodic), whereas electron transfer in the opposite direction results in the reduction of the species (cathodic). Electron transfer is only possible when the electroactive material is within molecular distances of the electrode surface thus for a simple electrode reaction involving solution species of the fonn... 

In adsorptive stripping voltammetry the deposition step occurs without electrolysis. Instead, the analyte adsorbs to the electrode s surface. During deposition the electrode is maintained at a potential that enhances adsorption. For example, adsorption of a neutral molecule on a Hg drop is enhanced if the electrode is held at -0.4 V versus the SCE, a potential at which the surface charge of mercury is approximately zero. When deposition is complete the potential is scanned in an anodic or cathodic direction depending on whether we wish to oxidize or reduce the analyte. Examples of compounds that have been analyzed by absorptive stripping voltammetry also are listed in Table 11.11. 

F r d ic Current. The double layer is a leaky capacitor because Faradaic current flows around it. This leaky nature can be represented by a voltage-dependent resistance placed in parallel and called the charge-transfer resistance. Basically, the electrochemical reaction at the electrode surface consists of four thermodynamically defined states, two each on either side of a transition state. These are (11) (/) oxidized species beyond the diffuse double layer and n electrons in the electrode and (2) oxidized species within the outer Helmholtz plane and n electrons in the electrode, on one side of the transition state and (J) reduced species within the outer Helmholtz plane and (4) reduced species beyond the diffuse double layer, on the other. 

There is a third real reason for deviations from Eq. (5.18) in the case that a non-conductive insulating product layer is built via a catalytic reaction on the catalyst electrode surface (e.g. an insulating carbonaceous or oxidic layer). This is manifest by the fact that C2H4 oxidation under fuel-rich conditions has been found to cause deviations from Eq. (5.18) while H2 oxidation does not. A non-conducting layer can store electric charge and thus the basic Eq. 5.29 (which is equivalent to Eq. (5.18)) breaks down. 

In a similar way, electrochemistry may provide an atomic level control over the deposit, using electric potential (rather than temperature) to restrict deposition of elements. A surface electrochemical reaction limited in this manner is merely underpotential deposition (UPD see Sect. 4.3 for a detailed discussion). In ECALE, thin films of chemical compounds are formed, an atomic layer at a time, by using UPD, in a cycle thus, the formation of a binary compound involves the oxidative UPD of one element and the reductive UPD of another. The potential for the former should be negative of that used for the latter in order for the deposit to remain stable while the other component elements are being deposited. Practically, this sequential deposition is implemented by using a dual bath system or a flow cell, so as to alternately expose an electrode surface to different electrolytes. When conditions are well defined, the electrolytic layers are prone to grow two dimensionally rather than three dimensionally. ECALE requires the definition of precise experimental conditions, such as potentials, reactants, concentration, pH, charge-time, which are strictly dependent on the particular compound one wants to form, and the substrate as well. The problems with this technique are that the electrode is required to be rinsed after each UPD deposition, which may result in loss of potential control, deposit reproducibility problems, and waste of time and solution. Automated deposition systems have been developed as an attempt to overcome these problems. 

Let s look at the little strip cartoon in Figure 7.7, which shows the surface of a copper electrode. For clarity, we have drawn only one of the trillion or so atoms on its surface. When the cell of which it is a part is permitted to discharge spontaneously, the copper electrode acquires a negative charge in consequence of an oxidative electron-transfer reaction (the reverse of Equation (7.7)). During the oxidation, the surface-bound atom loses the two electrons needed to bond the atom to the electrode surface, becomes a cation and diffuses into the bulk of the solution. 

Finally, we should note that the extent of oxidation or reduction needed to cause a surface charge of this type need not be large and the acquisition of charge, whether positive or negative, is fast and requires no more than a millisecond after immersing the electrodes in their respective half-cells. 

---