Film blowing products

The film thickness produced by film blowing ranges from 10 /mi to 100 pm and the rates of production are very high. The most common plastic films produced by this method are branched LDPE, linear low density polyethylene (LLDPE), and linear HDPE films. By using more than one extruder, multilayer films can also be manufactured. To appreciate the... [Pg.836]

EVOH have superior gas barrier properties.80 89 They are often used as the internal layer in multilayer food packaging films, blow molded rigid containers, gasoline tanks for automobiles for a variety of purposes, etc. EVOH can be fabricated by the usual melt processing methods. The barrier properties of films decrease in the presence of moisture, so multilayer with protective polypropylene (especially biaxially oriented material), low-density polyethylene, nylons, or other moisture barrier films provides films or products that are useful even with liquids. The... [Pg.72]

Products Homopolymers and copolymers are produced for applications in film, blow molding, injection molding, roto molding, pipe, sheet and thermoforming, and wire and cable. [Pg.89]

Products Polymer density is easily controlled from 0.915 to 0.970 g/cm. Depending on catalyst type, molecular weight distribution is either narrow or broad. Melt index maybe varied from less than 0.1 to greater than 200. Grades suitable for film, blow-molding, pipe, roto-molding and extrusion applications are produced. [Pg.90]

The SH plays a positive role in film blowing (15, 44) or in wire coating ( ). LPX-30 does not show this effect and Its processability Index Is low. On the other hand, SH of LDPE Is quite high and so Is the processability Index. The accepted mechanism for Improvement of fllm bubble stability Is self healing of a potentially weak spot by a local Increase of extenslonal viscosity caused by SH. It Is Important to note that adding to LPX-30 either 10 wtZ LDPE, 202 LLDPE-10 or lOZ LPX-24 was sufficient for generation of SH. The subsequent trial on a production line confirmed these results Increased bubble stability allowed for higher production rates of the blends. [Pg.176]

Beilstein Handbook Reference) AI3-02247 BRN 1912251 Dimethyl 1,3-benzenedi-carboxylate Dimethyl isophthalate Dimethyl m-phthalate Dimethylester kyseliny isoftalove EINECS 215-951-9 HSDB 6138 Isophthalic acid dimethyl ester Methyl 3-(carbomethoxy)benzoate Methyl isophthalate Morflex 1129 NSC 15313 Uniplex 270. Chemical intermediate in the synthesis of polyesters. Used as a plasticizer, modifies clarity and melting point of PET resins used in films, blow-molded bottles, and similar products. Needles mp = 67.5° bp = 282° d = 1.194 Xm = 280, 288 nm (MeOH) slightly soluble in H2O, Morfiex Unitex. [Pg.231]

There are several methods for the production of polymeric films (see Table 9.18). The oldest is calendering, but the most common methods are the film blowing and sheet extrusion. Others can be made by post-treating the extruded sheet, e.g., polyimide films [Sweeting, 1971]. Polymer films can also be polymerized onto a substrate from monomers in the vapor state, or formed by the coalescence of polymer dispersions. However, several polymers caimot be formed without dissolving them. [Pg.625]

PBS is a typical thermoplastic and can be processed via various methods, such as extrusion, injection molding, film blowing, fiber spinning, and thermoforming. It has been reported that PBS can be processed into melt-blown, multifilament, monofilament, nonwoven, flat and split yarn, injection-molded products, film, paper laminate, sheet, and tape for applications in the textile and plastic industries. [Pg.363]

Polystyrenes are mostly extruded and injection molded to get to the final shape of the products. However, polystyrenes can also form sheets by physical processes such as film blowing and stretching to obtain polystyrene film. In the... [Pg.342]

P = 10-40 MPa in the presence of Al(Ci 2, or 4)3] leads to PE having a relatively broad MWD, p = 0.910-0.935 g mL and good processability. The PE is suitable Pot the preparation of blown or cast films, blow-molded parts, extruded goods, and injection-molded products... [Pg.1663]


See other pages where Film blowing products is mentioned: [Pg.523]    [Pg.700]    [Pg.837]    [Pg.271]    [Pg.26]    [Pg.251]    [Pg.199]    [Pg.145]    [Pg.507]    [Pg.521]    [Pg.654]    [Pg.732]    [Pg.735]    [Pg.736]    [Pg.736]    [Pg.1156]    [Pg.1157]    [Pg.217]    [Pg.220]    [Pg.394]    [Pg.114]    [Pg.124]    [Pg.497]    [Pg.205]    [Pg.96]    [Pg.13]    [Pg.20]    [Pg.135]    [Pg.153]    [Pg.226]    [Pg.402]    [Pg.445]    [Pg.5]    [Pg.112]    [Pg.91]    [Pg.825]    [Pg.847]    [Pg.1563]    [Pg.322]   