Conducting polymers redox doping

The stoichiometry of the redox reactions of conducting polymers (n and m in reactions 1 and 2) is quite variable. Under the most widely used conditions, polypyrroles and polythiophenes can be reversibly oxidized to a level of one hole per ca. 3 monomer units (i.e., a degree of oxidation, n, of ca. 0.3).7 However, this limit is dictated by the stability of the oxidized film under the conditions employed (Section V). With particularly dry and unreactive solvents, degrees of oxidation of 0.5 can be reversibly attained,37 and for poly-(4,4 -dimethoxybithiophene), a value of n = 1 has been reported.38 Although much fewer data are available for n-doping, it appears to involve similar stoichiometries [i.e., m in Eq. (2) is typically ca. 0.3].34,39"41 Polyanilines can in principle be reversibly p-doped to one... 

Figure 4 compares cyclic voltammograms for a redox polymer (poly-[Fe(5-amino-1,10-phenanthroline)3]3+/2+)91 and p-doping and undoping of a conducting polymer (polypyrrole).92 The voltammogram for the redox... 

Figure 4. (A) Cyclic voltammograms over a range of scan rates for a redox polymer (poly-[Fe 5-amino-1,10-phenanthrotme)3]3+/>)91 and (B) p-doping and undoping of a conducting polymer (polypyrrole) (B). [(A) Reprinted from X. Ren and P. O. Pickup, Strong dependence of the election hopping rate in poly-tris(5-amino-1,10-phenan-throline)iron(HI/II) on the nature of the counter-anion J. Electroanal. Chem. 365, 289-292,1994, with kind permission from Elsevier Sciences S.A.]...

Intensive research on the electrocatalytic properties of polymer-modified electrodes has been going on for many years Until recently, most known coatings were redox polymers. Combining redox polymers with conducting polymers should, in principle, further improve the electrocatalytic activity of such systems, as the conducting polymers are, in addition, electron carriers and reservoirs. One possibility of intercalating electroactive redox centres in the conducting polymer is to incorporate redoxactive anions — which act as dopants — into the polymer. Most research has been done on PPy, doped with inter alia Co 96) RyQ- 297) (--q. and Fe-phthalocyanines 298,299) Co-porphyrines Evidently, in these... 

Electrochemical oxidation of X produces a polymer film with polythiophene as the backbone and viologen centers as pendant redox groups. The electrochemical properties of the polymer are the combination of polythiophene and viologen. Using viologen subunits as the internal standard (one per repeat unit of the polymer), the "doping level" of the oxidized polythiophene backbone at its maximum conductivity can be measured and is about 25%. The charge transport via the pendant V2+/+ of poly(l) has been studied by... 

---