Nitridation reactions ceramic powder synthesis

This chapter discusses the fluid-solid and solid-solid reactions used to produce ceramic powders. The first aspect of this discussion is the spontaneity of a particular reaction for a given temperature and atmosphere. Thermodynamics is used to determine whether a reaction is spontaneous. The thermod3mamics of the thermal decomposition of minerals and metal salts, oxidation reactions, reduction reactions, and nitridation reactions is discussed because these are often used for ceramic powder synthesis. After a discussion of thermodynamics, the kinetics of reaction is given to determine the time necessary to complete the reaction. Reaction kinetics are discussed in terms of the various rate determining steps of mass and heat transfer, as well as surface reaction. After this discussion of reaction kinetics, a brief discussion of the types of equipment used for the synthesis of ceramic powders is presented. Finally, the kinetics of solid—solid interdiffusion is discussed. 

The reduction of oxides in reducing atmospheres is also an important industrial fluid—solid reaction that produces a powder. Because these types of reactions can affect ceramic powder synthesis, they are included in this chapter. However, these reduction reactions are frequently used to produce metal powders and are not often used to produce ceramic powders. These reduction reaction can, however, be the first step in a sequence of steps to produce carbide and nitride powders. Several examples of fluid—solid reduction reactions are... 

Vapor-Phase Techniques. Vapor-phase powder synthesis teclmiques, including vapor condensation, vapor decomposition, and vapor—vapor, vapor—Hquid, and vapor—soHd reactions, employ reactive vapors or gases to produce high purity, ultrafine, reactive ceramic powders. Many nonoxide powders, eg, nitrides and carbides, for advanced ceramics are prepared by vapor-phase synthesis. 

Vapor—vapor reactions (14,16,17) are responsible for the majority of ceramic powders produced by vapor-phase synthesis. This process iavolves heating two or more vapor species which react to form the desired product powder. Reactant gases can be heated ia a resistance furnace, ia a glow discharge plasma at reduced pressure, or by a laser beam. Titania [13463-67-7] Ti02, siUca, siUcon carbide, and siUcon nitride, Si N, are among some of the technologically important ceramic powders produced by vapor—vapor reactions. 

Vapor—sohd reactions (13—17) are also commonly used ia the synthesis of specialty ceramic powders. Carbothermic reduction of oxides, ia which carbon (qv) black mixed with the appropriate reactant oxide is heated ia nitrogen or an iaert atmosphere, is a popular means of produciag commercial SiC, Si N, aluminum nitride [24304-00-3], AIN, and sialon, ie, siUcon aluminum oxynitride, powders. 

---