Reactions of HCl and nitrides, borides, silicides, germanides, carbides, and sulfides take place at significant rates only at elevated (>650° C) temperatures. The products are the metal chlorides and the corresponding hydrides. The reactions most studied are those involving nitrides of aluminum, magnesium, calcium, and titanium, where ammonia (qv) is formed along with the corresponding metal chloride. 

Preparation. The simplest method of preparation is a combination of the elements at a suitable temperature, usually ia the range of 1100—2000°C. On a commercial scale, borides are prepared by the reduction of mixtures of metallic and boron oxides usiag aluminum, magnesium, carbon, boron, or boron carbide, followed by purification. Borides can also be synthesized by vapor-phase reaction or electrolysis. 

Most structural PMCs consist of a relatively soft matrix, such as a thermosetting plastic of polyester, phenolic, or epoxy, sometimes referred to as resin-matrix composites. Some typical polymers used as matrices in PMCs are listed in Table 1.28. The list of metals used in MMCs is much shorter. Aluminum, magnesium, titanium, and iron- and nickel-based alloys are the most common (see Table 1.29). These metals are typically utilized due to their combination of low density and good mechanical properties. Matrix materials for CMCs generally fall into fonr categories glass ceramics like lithium aluminosilicate oxide ceramics like aluminnm oxide (alnmina) and mullite nitride ceramics such as silicon nitride and carbide ceramics such as silicon carbide. 

Metals and ceramics (claylike materials) are also used as matrices in advanced composites. In most cases, metal matrix composites consist of aluminum, magnesium, copper, or titanium alloys of these metals or intermetallic compounds, such as TiAl and NiAl. The reinforcement is usually a ceramic material such as boron carbide (B4C), silicon carbide (SiC), aluminum oxide (A1203), aluminum nitride (AlN), or boron nitride (BN). Metals have also been used as reinforcements in metal matrices. For example, the physical characteristics of some types of steel have been improved by the addition of aluminum fibers. The reinforcement is usually added in the form of particles, whiskers, plates, or fibers. 

The saltlike carbides formed from beryllium (Be2C) and from aluminum (AI4C3) are best described as methides they yield methane upon hydrolysis, and the carbon atoms have been found to be far enough apart from each other to preclude any type of carbon-carbon binding. One of the two carbides of magnesium has the composition Mg2C3 and yields methylacetylene, CH3C=CH, upon hydrolysis the carbide anion here is presumably [-3C—C=C <-> 20=C=C-2]. 

FERRIC OXIDE (1309-37-1) FcjO, Violent reactions with powdered aluminum (thermite reaction), hydrogen peroxide, calcium disilicide (thermite reaction), ethylene oxide (may cause explosive polymerization), calcium hypochlorite, hydrazine, hydrogen trisulfide, powdered magnesium. Contact with carbon monoxide may cause fire or explosion. Incompatible with calcium carbide (powdered), chlorides, guanidinium perchlorate, metal acetylides. Contact with the explosive hydrazinium diperchlorate or ammonium perchlorate can increase heat-, mechanical shock-, or friction sensitivity. Incompatible with aluminum-magnesium-zinc alloys. Spent material... 

Carbon bricks are also used as linings for furnaces making phosphorus, calcium carbide, aluminum, and magnesium. In some arc furnaces, the arc is struck between the electrodes and the hearth. In those cases, carbon bricks are used to make the hearth conduct heat. 

The superalloys, as well as alloys of aluminum, magnesium, titanium, and copper, are used as matrix materials. The reinforcement may be in the form of particulates, both continuous and discontinuous fibers, and whiskers concentrations normally range between 10 and 60 vol%. Continuous-fiber materials include carbon, silicon carbide, boron, aluminum oxide, and the refractory metals. However, discontinuous reinforcements consist primarily of silicon carbide whiskers, chopped fibers of aluminum oxide and carbon, or particulates of silicon carbide and aluminum oxide. In a sense, the cermets (Section 16.2) fall within this MMC scheme. Table 16.9 presents the properties of several common metal-matrix, continuous and aligned fiber-reinforced composites. 

Iodine Acetaldehyde, acetylene, aluminum, ammonia (aqueous or anhydrous), antimony, bromine pentafluoride, carbides, cesium oxide, chlorine, ethanol, fluorine, formamide, lithium, magnesium, phosphorus, pyridine, silver azide, sulfur trioxide... 

Sihca is reduced to siUcon at 1300—1400°C by hydrogen, carbon, and a variety of metallic elements. Gaseous siUcon monoxide is also formed. At pressures of >40 MPa (400 atm), in the presence of aluminum and aluminum haUdes, siUca can be converted to silane in high yields by reaction with hydrogen (15). SiUcon itself is not hydrogenated under these conditions. The formation of siUcon by reduction of siUca with carbon is important in the technical preparation of the element and its alloys and in the preparation of siUcon carbide in the electric furnace. Reduction with lithium and sodium occurs at 200—250°C, with the formation of metal oxide and siUcate. At 800—900°C, siUca is reduced by calcium, magnesium, and aluminum. Other metals reported to reduce siUca to the element include manganese, iron, niobium, uranium, lanthanum, cerium, and neodymium (16). 

Sihcon carbide is comparatively stable. The only violent reaction occurs when SiC is heated with a mixture of potassium dichromate and lead chromate. Chemical reactions do, however, take place between sihcon carbide and a variety of compounds at relatively high temperatures. Sodium sihcate attacks SiC above 1300°C, and SiC reacts with calcium and magnesium oxides above 1000°C and with copper oxide at 800°C to form the metal sihcide. Sihcon carbide decomposes in fused alkahes such as potassium chromate or sodium chromate and in fused borax or cryohte, and reacts with carbon dioxide, hydrogen, ak, and steam. Sihcon carbide, resistant to chlorine below 700°C, reacts to form carbon and sihcon tetrachloride at high temperature. SiC dissociates in molten kon and the sihcon reacts with oxides present in the melt, a reaction of use in the metallurgy of kon and steel (qv). The dense, self-bonded type of SiC has good resistance to aluminum up to about 800°C, to bismuth and zinc at 600°C, and to tin up to 400°C a new sihcon nitride-bonded type exhibits improved resistance to cryohte. 

---