The living character of organolithium polymerizations makes such processes ideally suited for the preparation of pure as well as tapered-block copolymers. Diene-olefin pure-block copolymers have become important commodities because of their unique structure-property relationships. When such copolymers have an ABA or (AB) X [A = polyolefin, e.g., polystyrene or poly(a-methylstyrene) B = polydiene, e.g., polybutadiene or polyisoprene and X = coupling-agent residue] arrangement of the blocks, the copolymers have found use as thermoplastic elastomers (i.e., elastomers that can be processed as thermoplastics). [Pg.81]

GopolymeriZation Initiators. The copolymerization of styrene and dienes in hydrocarbon solution with alkyUithium initiators produces a tapered block copolymer stmcture because of the large differences in monomer reactivity ratios for styrene (r < 0.1) and dienes (r > 10) (1,33,34). In order to obtain random copolymers of styrene and dienes, it is necessary to either add small amounts of a Lewis base such as tetrahydrofuran or an alkaU metal alkoxide (MtOR, where Mt = Na, K, Rb, or Cs). In contrast to Lewis bases which promote formation of undesirable vinyl microstmcture in diene polymerizations (57), the addition of small amounts of an alkaU metal alkoxide such as potassium amyloxide ([ROK]/[Li] = 0.08) is sufficient to promote random copolymerization of styrene and diene without producing significant increases in the amount of vinyl microstmcture (58,59). [Pg.239]

Tbe system may be used for homopolymers and for block copolymers. Some commercial SBS triblock thermoplastic rubbers and the closely related K-resins produced by Phillips are of this type. Anionic polymerisation methods are of current interest in the preparation of certain diene rubbers. [Pg.37]

ADMET is quite possibly the most flexible transition-metal-catalyzed polymerization route known to date. With the introduction of new, functionality-tolerant robust catalysts, the primary limitation of this chemistry involves the synthesis and cost of the diene monomer that is used. ADMET gives the chemist a powerful tool for the synthesis of polymers not easily accessible via other means, and in this chapter, we designate the key elements of ADMET. We detail the synthetic techniques required to perform this reaction and discuss the wide range of properties observed from the variety of polymers that can be synthesized. For example, branched and functionalized polymers produced by this route provide excellent models (after quantitative hydrogenation) for the study of many large-volume commercial copolymers, and the synthesis of reactive carbosilane polymers provides a flexible route to solvent-resistant elastomers with variable properties. Telechelic oligomers can also be made which offer an excellent means for polymer modification or incorporation into block copolymers. All of these examples illustrate the versatility of ADMET. [Pg.435]

NR, styrene-butadiene mbber (SBR), polybutadiene rubber, nitrile mbber, acrylic copolymer, ethylene-vinyl acetate (EVA) copolymer, and A-B-A type block copolymer with conjugated dienes have been used to prepare pressure-sensitive adhesives by EB radiation [116-126]. It is not necessary to heat up the sample to join the elastomeric joints. This has only been possible due to cross-linking procedure by EB irradiation [127]. Polyfunctional acrylates, tackifier resin, and other additives have also been used to improve adhesive properties. Sasaki et al. [128] have studied the EB radiation-curable pressure-sensitive adhesives from dimer acid-based polyester urethane diacrylate with various methacrylate monomers. Acrylamide has been polymerized in the intercalation space of montmorillonite using an EB. The polymerization condition has been studied using a statistical method. The product shows a good water adsorption and retention capacity [129]. [Pg.866]

We have considerable latitude when it comes to choosing the chemical composition of rubber toughened polystyrene. Suitable unsaturated rubbers include styrene-butadiene copolymers, cis 1,4 polybutadiene, and ethylene-propylene-diene copolymers. Acrylonitrile-butadiene-styrene is a more complex type of block copolymer. It is made by swelling polybutadiene with styrene and acrylonitrile, then initiating copolymerization. This typically takes place in an emulsion polymerization process. [Pg.336]

Thermoplastic elastomeric behavior requires that the block copolymer develop a microheterogeneous two-phase network morphology. Theory predicts that microphase separation will occur at shorter block lengths as the polarity difference between the A and B blocks increases. This prediction is borne out as the block lengths required for the polyether-polyurethane, polyester-polyurethane, and polyether-polyester multiblock copolymers to exhibit thermoplastic elastomeric behavior are considerably shorter than for the styrene-diene-styrene triblock copolymers. [Pg.31]

Poly(l,4-naphthylenevinylenes) have been prepared by metathesis polymerization of benzobarrelenes [181,182] and the photoluminescence properties of homopolymers and block-copolymers have been studied in some detail [183]. PPV also has been prepared via ROMP of [2.2]paracyclophane-l,9-diene [184] and ROMP of a paracyclophene that contains a solubilizing leaving group [185]. The resulting polymer is converted to PPV upon acid catalysis at room temperature. ADMET of 2,5-dialkyl-l,4-divinylbenzenes using Mo or W catalysts has... [Pg.31]

Styrene copolymer foams, 23 404 Styrene copolymers, 23 366-367 properties of, 10 206t Styrene derivative polymers, 23 367-368 Styrene derivatives, 23 348-355 Styrene-diene block copolymers, 14 251 Styrene-divinylbenzene copolymers,... [Pg.894]

Excellent reviews on micelles formed in organic solvents have been published by Hamley [2], Chu et al. [86], and Riess [14]. From these overviews it appears that a wide range of styrene-, (meth)acrylates-, and dienes-based block copolymers were investigated and that the formation of micelles in organic solvents can generally be considered as an entropy-driven process. AB diblock and ABA triblock architectures were systematically compared. All these previous investigations have been summarized by Hamley [2], We will therefore not perform an extensive review of all these systems, since this information has already been provided by others, but we will briefly outline some selected examples. [Pg.96]

The additional complexity present in block copolymer synthesis is the order of monomer polymerization and/or the requirement in some cases to modify the reactivity of the propagating center during the transition from one block to the next block. This is due to the requirement that the nucleophilicity of the initiating block be equal or greater than the resulting propagating chain end of the second block. Therefore the synthesis of block copolymers by sequential polymerization generally follows the order dienes/styrenics before vinylpyridines before meth(acrylates) before oxiranes/siloxanes. As a consequence, styrene-MMA block copolymers should be prepared by initial polymerization of styrene followed by MMA, while PEO-MMA block copolymers should be prepared by... [Pg.50]

The chromatogram of Kraton 1107 shows the other components of the sample besides the major coupled diene S-l-l-S small amounts of "kill" polystyrene, uncoupled S-1 block copolymer, and material with higher molecular weight than that of SlIS are indicated. As indicated in Figures 2a and 3a, the LB polymers all showed a small polystyrene "kill" component and a high molecular weight shoulder on the block copolymer peak with a molecular weight of about twice that of the block copolymer. [Pg.315]

Thus, the synthesis of a styrene-methyl methacrylate block polymer requires that styrene be the first monomer. Further, it is useful to decrease the nucleophilicity of polystyryl carbanions by adding a small amount of 1,1-diphenylethene to minimize attack at the ester function of MMA [Quirk et al., 2000]. Block copolymers of styrene with isoprene or 1,3-butadiene require no specific sequencing since crossover occurs either way. Block copolymers of MMA with isoprene or 1,3-butadiene require that the diene be the first monomer. The length of each segment in a block copolymer is controlled by the ratio of each monomer to initiator. The properties of the block copolymer vary with the block lengths of the different monomers. [Pg.437]

Difunctional initiators such as sodium naphthalene are useful for producing ABA, BABAB, CAB AC, and other symmetric block copolymers more efficiently by using fewer cycles of monomer additions. Difunctional initiators can also be prepared by reacting a diene such as /n-diisoprope ny I benzene or l,3-bis(l-phenylethenyl)benzene with 2 equiv of butyl-lithium. Monomer B is polymerized by a difunctional initiator followed by monomer A. A polymerizes at both ends of the B block to form an ABA triblock. BABAB or CABAC block copolymers are syntehsized by the addition of monomer B or C to the ABA living polymer. The use of a difunctional initiator is the only way to synthesize a MMA-styrene-MMA triblock polymer since MMA carbanion does not initiate styrene polymerization (except by using a coupling reaction—Sec. 5-4c). [Pg.437]

In addition to the triblock thermoplastic elastomers, other useful copolymers of styrene with a diene are produced commerically by living anionic polymerization. These include di-and multiblock copolymers, random copolymers, and tapered block copolymers. A tapered (gradient) copolymer has a variation in composition along the polymer chain. For example, S-S/D-D is a tapered block polymer that tapers from a polystyrene block to a styrene-diene random copolymer to polydiene block. (Tapered polymers need not have pure blocks at their ends. One can have a continuously tapered composition from styrene to diene by... [Pg.437]

Several polymers based on 1,3-dienes are used as elastomers. These include styrene-1,3-butadiene (SBR), styrene-1,3-butadiene terpolymer with an unsaturated carboxylic acid (carboxylated SBR), acrylonitrile-1,3-butadiene (NBR or nitrile rubber) (Secs. 6-8a, 6-8e), isobutylene-isoprene (butyl rubber) (Sec. 5-2i-l), and block copolymers of isoprene or... [Pg.699]

In general, block copolymers are heterogeneous (multiphase) polymer systems, because the different blocks from which they are built are incompatible with each other, as for example, in diene/styrene-block copolymers. This incompatibility, however, does not lead to a complete phase separation because the polystyrene segments can aggregate with each other to form hard domains that hold the polydiene segments together. As a result, block copolymers often combine the properties of the relevant homopolymers. This holds in particular for block copolymers of two monomers A and B. [Pg.150]

A second route is termed sequential anionic polymerization. More recently, also controlled radical techniques can be applied successfully for the sequential preparation of block copolymers but still with a less narrow molar mass distribution of the segments and the final product. In both cases, one starts with the polymerization of monomer A. After it is finished, monomer B is added and after this monomer is polymerized completely again monomer A is fed into the reaction mixture. This procedure is applied for the production of styrene/buta-diene/styrene and styrene/isoprene/styrene triblock copolymers on industrial scale. It can also be used for the preparation of multiblock copolymers. [Pg.251]

Only a limited number of monomer pairs form block copolymers in this manner. Examples are conjugated dienes and vinyl aromatics that have similar Q-e values. The nature of the anionic initiator, i.e., the ionic character of the carbon-metal bond plays an important role in both the amount and sequence of block formation. For instance, when potassium or cesium initiators are used, styrene polymerizes first as can be seen in Figure 12. [Pg.397]

So far the discussion was focused on copolymers derived from a mixture of styrene and a diene. In view of the "living" nature of organolithium polymerization, it is also possible to synthesize block polymers in which the sequence and length of the blocks are controlled by incremental (or sequential) addition of monomersr This general method of preparing block polymers is readily adaptable to commercial production, and, indeed, a number of block copolymers are manufactured this way. Those that have received the most attention in recent years are the diene-styrene two-phase... [Pg.401]


See other pages where Block copolymers dienes is mentioned: [Pg.239]    [Pg.12]    [Pg.566]    [Pg.282]    [Pg.77]    [Pg.103]    [Pg.107]    [Pg.137]    [Pg.141]    [Pg.207]    [Pg.259]    [Pg.483]    [Pg.19]    [Pg.88]    [Pg.487]    [Pg.39]    [Pg.53]    [Pg.12]    [Pg.191]    [Pg.548]    [Pg.158]    [Pg.296]    [Pg.106]    [Pg.403]    [Pg.437]    [Pg.23]    [Pg.432]    [Pg.404]    [Pg.411]   
See also in sourсe #XX -- [ Pg.865 , Pg.866 ]




SEARCH



Copolymers, block styrene-diene microstructure

DIENE COPOLYMER

Diene-acrylic block copolymers

Diene-acrylic block copolymers synthesis

Polypropylene diene block copolymers

Styrene-diene block copolymers

© 2024 chempedia.info