Ziegler Natta syndiospecific propagation

Furthermore, studies of the microstructure of copolymers formed by the low-temperature copolymerisation of cis-1 -(2 H)-propene (or trans isomer) and perdeuteropropene in the presence of soluble vanadium-based Ziegler-Natta catalysts showed syndiospecific propagation to involve a monomer insertion of the cis type [27]. 

Syndiospecific Propagation Reaction Stereocontrol in the Presence of Soluble Vanadium-based Ziegler-Natta Catalysts... 

The same conclusion as in the case of propylene homopolymerisation has been drawn considering IR [396] and NMR [389,395] spectra of ethylene/propylene copolymers obtained with vanadium-based syndiospecific catalysts. The type of propylene insertion depends on the kind of last inserted monomer unit secondary insertion [scheme (40)] occurs more frequently when the last monomeric unit of the growing chain is propylene, while primary propylene insertion [scheme (39)] is more frequent when the last monomeric unit of the growing chain is ethylene [2]. The above explains the microstructure of ethylene/propylene copolymers obtained with vanadium-based Ziegler-Natta catalysts. These copolymers contain both m and r diads when the sequence of propylene units is interrupted by isolated ethylene units i.e. a propylene insertion after an ethylene insertion is substantially non-stereospecific [327,390,397], The existence of a steric interaction between the incoming monomer molecule and the last added monomer unit is also confirmed by the fact that the propagation rate for the secondary insertion of propylene in syndiospecific polymerisation is lower than for primary insertion in non-stereospecific polymerisation [398],... 

Zam belli and Tosi have extensively studied the stereochemistry of the propagation step in propylene polymerization on Ziegler-Natta catalysts. Specific features of this process are shown in Table 4. Cis-addition of the olefin to the active metal-carbon bond has been observed both in isospecific and syndiospecific polymerization. The olefin addition to the active bond proceeds with the participation of the primary (L,(Mt—CH2—CHR—P) and secondary (L,Mt—CHR—CH2—P) carbon atoms of the growing polymer chain using isospecific and syndiospecific catalysts, respectively. 

---