Styrene-methacrylic anhydride cyclization constants

Several theoretical treatments of cyclocopolymerization have been reported previously (8-11). These relate the compositions of cyclocopolymers to monomer feed concentrations and appropriate rate constant ratios. To our knowledge, procedures for calculating sequence distributions for either cyclocopolymers or for copolymers derived from them have not been developed previously. In this paper we show that procedures for calculating sequence distributions of terpolymers can be used for this purpose. Most previous studies on styrene-methacrylic anhydride copolymerizations (10,12,13) have shown that a high proportion of the methacrylic anhydride units are cyclized in these polymers. Cyclization constants were determined from monomer feed concentrations and the content of uncyclized methacrylic anhydride units in the copolymers. These studies invoked simplifying assumptions that enabled the conventional copolymer equation to be used in determinations of monomer reactivity ratios for this copolymerization system. 

Due to the difficulty of working with styrene-methacrylic anhydride copolymers, we have elected to determine reactivity ratios and cyclization constants from the compositions and structures of styrene-MMA copolymers derived from these copolymers. As is discussed in the experimental section it is possible to measure the styrene contents and the proportions of methoxy proton resonance occurring in three different areas (designated A, B and C) from the 1H-NMR spectra of S/MMA copolymers. The proportions of methoxy proton resonance observed in the A (F ), B (Fjj) and C (Fc) areas obey the following relationships in conventional styrene-MMA copolymers (6 7). 

Reactivity Ratios and Cyclization Constants Estimated for Styrene-Methacrylic Anhydride Copolymerization... 

These equations are similar to those assumed for the reactivity ratio determination. In contrast to what has been observed for conventional styrene-MMA copolymers, however, these equations indicate that a substantial proportion of the (SMM+MMS)-type resonance appears to occur in the C-area. The proportion of methoxy resonance observed in the C-area, in fact, exceeds P(SMS) by a substantial amount for many of the copolymers. This can be due to the assumption of an inadequate model for the copolymerization reaction, to the use of incorrect reactivity ratios and cyclization constants for the calculations or to an inadequate understanding of the methoxy proton resonance patterns of S/MMA copolymers. It is possible that intramolecular reactions between propagating radicals and uncyclized methacrylic anhydride units present on propagating chains result in the formation of macrocycles. Failure to account for the formation of macrocycles would result in overestimation of rc and rc and in underestimation of the proportions of MMA units in SMS triads in the derived S./MMA copolymers. This might account for the results obtained. An alternate possibility is that a high proportion (>50%) of the M-M placements in the copolymers studied in this work can be expected to have meso placements (], J2), whereas only a small proportion of such placements ( 20%) are meso in conventional S/MMA copolymers. Studies with molecular models (20) have indicated that the methoxy protons on MMA units centered in structures such as the following can experience appreciable shielding by next nearest styrene units. 

---