Soapless emulsion process

According to the other kinetic model proposed for the soapless emulsion process, the growing macroradicals may also form micelle structures at earlier polymerization times since they have both a hydrophilic end coming from the initiator and a hydrophobic chain [74]. 

When the emulsion polymerization is conducted in the absence of an emulsifier, this process is termed emulsifier free or soapless emulsion polymerization [68-73]. In this case, the particle formation occurs by the precipitation of growing macroradicals within the continuous... 

The soapless seeded emulsion copolymerization method was used for producing uniform microspheres prepared by the copolymerization of styrene with polar, functional monomers [115-117]. In this series, polysty-rene-polymethacrylic acid (PS/PMAAc), poly sty rene-polymethylmethacrylate-polymethacrylic acid (PS/ PMMA/PMAAc), polystyrene-polyhydroxyethylmeth-acrylate (PS/PHEMA), and polystyrene-polyacrylic acid (PS/PAAc) uniform copolymer microspheres were synthesized by applying a multistage soapless emulsion polymerization process. The composition and the average size of the uniform copolymer latices prepared by multistage soapless emulsion copolymerization are given in Table 11. 

Soapless seeded emulsion copolymerization has been proposed as an alternative method for the preparation of uniform copolymer microspheres in the submicron-size range [115-117]. In this process, a small part of the total monomer-comonomer mixture is added into the water phase to start the copolymerization with a lower monomer phase-water ratio relative to the conventional direct process to prevent the coagulation and monodispersity defects. The functional comonomer concentration in the monomer-comonomer mixture is also kept below 10% (by mole). The water phase including the initiator is kept at the polymerization temperature during and after the addition of initial monomer mixture. The nucleation takes place by the precipitation of copolymer macromolecules, and initially formed copolymer nuclei collide and form larger particles. After particle formation with the initial lower organic phase-water ratio, an oligomer initiated in the continuous phase is... 

---