Polyether plastics polyphenylene oxide

Flame resistance The underwriters ruling on the use of self-extinguishing plastics for contact-carrying members and many other components introduces critical material selection problems. All TSs are basically self-extinguishing. Nylon, polyphenylene oxide, polysulfone, polycarbonate, vinyl, chlorinated polyether, chlorotrifluoroethy-lene, vinylidene fluoride, and fluorocarbon are examples of TPs that may be suitable for applications requiring self-extinguishing properties. Cellulose acetate and ABS are also available with these properties. Glass reinforcement improves these materials considerably. 

Moisture Deteriorating effects of moisture are well known as reviewed early in this chapter (OTHER BEHAVIOR, Drying Plastic). Examples for high moisture applications include polyphenylene oxide, polysulfone, acrylic, butyrate, diallyl phthalate, glass-bonded mica, mineral-filled phenolic, chlorotrifluoroethylene, vinylidene, chlorinated polyether chloride, vinylidene fluoride, and fluorocarbon. Diallyl phthalate, polysulfone, and polyphenylene oxide have performed well with moisture/steam on one side and air on the other (a troublesome... 

To the range of engineering plastics were added polyethylene and polybutylene tereph-thalates (PET and PBT), as well as General Electric s polyethers, the PPO (polyphenylene oxide) produced through polymerization of 2,6-xylenol and the Noryl plastic produced by blending PPO with polystyrene. Other special polymers, derived like the polycarbonates from bisphenol A, were added to this range polyarylates, polysul-fones, polyetherimides. 

Fortunately, the deficiencies of both the classic thermosets and general purpose thermoplastics have been overcome by the commercialization of a series of engineering plastics including polyacetals, polyamides, polycarbonate, polyphenylene oxide, polyaryl esters, polyaryl sulfones, polyphenylene sulfide, polyether ether ketones and polylmides. Many improvements in performance and processing of these new polymers may be anticipated through copolymerization, blending and the use of reinforcements. 

---