Titanates have been instrumental in the bonding of fluorinated resins to packaging films, poly(hydantoin)—polyester to polyester wire enamel, polysulfide sealant to polyurethane (a phosphated titanate is recommended), polyethylene to cellophane using a titanated polyethylenimine, and silicone mbber sealant to metal or plastic support using polysilane (Si—H) plus polysiloxane (Si—OR) and titanate as the adhesive ingredients (450—454). Polyester film coated first with a titanium alkoxide, then with a poly(vinyl alcohol)—polyethylenimine blend, becomes impermeable to gases (455). 

Textiles used as fabric fagades are commonly a coated mesh. This allows a view out and reduces energy consumption while providing solar protection (Armijos, 2008). The most common types are PVC-coated polyester manufactured into a coated or extruded product, PTFE (poly-tetrafluoroethylene or Teflon) coated flbreglass mesh, and ETFE (ethylene-tetrafluoroethylene) foils. 

Acrylics. Acetone is converted via the intermediate acetone cyanohydrin to the monomer methyl methacrylate (MMA) [80-62-6]. The MMA is polymerized to poly(methyl methacrylate) (PMMA) to make the familiar clear acryUc sheet. PMMA is also used in mol ding and extmsion powders. Hydrolysis of acetone cyanohydrin gives methacrylic acid (MAA), a monomer which goes direcdy into acryUc latexes, carboxylated styrene—butadiene polymers, or ethylene—MAA ionomers. As part of the methacrylic stmcture, acetone is found in the following major end use products acryUc sheet mol ding resins, impact modifiers and processing aids, acryUc film, ABS and polyester resin modifiers, surface coatings, acryUc lacquers, emulsion polymers, petroleum chemicals, and various copolymers (see METHACRYLIC ACID AND DERIVATIVES METHACRYLIC POLYMERS). 

Polyester. Poly(ethylene terephthalate) [25038-59-9] (PET) polyester film has intermediate gas- and water- vapor barrier properties, very high tensile and impact strengths, and high temperature resistance (see Polyesters, thermoplastic). AppHcations include use as an outer web in laminations to protect aluminum foil. It is coated with PVDC to function as the flat or sealing web for vacuum/gas flush packaged processed meat, cheese, or fresh pasta. 

Poly(vinylidene chloride). Poly(viayHdene chloride) [9002-85-1] (PVDC), most of which is produced by Dow Chemical, is best known in its saran or PVC-copolymerized form (see Vinylidene chloride and poly(VINYLIDENE chloride)). As solvent or emulsion coating, PVDC imparts high oxygen, fat, aroma, and water-vapor resistance to substrates such as ceUophane, oriented polypropylene, polyester, and nylon. 

AppHcation of an adhesion-promoting paint before metal spraying improves the coating. Color-coded paints, which indicate compatibiHty with specific plastics, can be appHed at 20 times the rate of grit blasting, typically at 0.025-mm dry film thickness. The main test and control method is cross-hatch adhesion. Among the most common plastics coated with such paints are polycarbonate, poly(phenylene ether), polystyrene, ABS, poly(vinyl chloride), polyethylene, polyester, and polyetherimide. 

Ionic polymers are also formulated from TDI and MDI (43). Poly(urethane urea) and polyurea ionomers are obtained from divalent metal salts of /)-aminohen2oic acid, MPA, dialkylene glycol, and 2,4-TDI (44). In the case of polyureas, the glycol extender is omitted. If TDI is used in coatings apphcations, it is usually converted to a derivative to lower the vapor pressure. A typical TDI prepolymer is the adduct of TDI with trimethyl olpropane (Desmodur L). Carbodiimide-modified MDI offers advantages in polyester-based systems because of improved hydrolytic stabihty (45). Moisture cure systems based on aromatic isocyanates are also available. 

A primary use of vinyhdene chloride copolymer lacquers is the coating of films made from regenerated ceUulose or of board or paper coated with polyamide, polyester, polypropylene, poly(vinyl chloride), and polyethylene. The lacquer imparts resistance to fats, oils, oxygen, and water vapor (165). 

Polyesters are eneountered in many forms. They are important as laminating resins, moulding compositions, fibres, films, surface coating resins, rubbers and plasticisers. The common factor in these widely different materials is that they all contain a number of ester linkages in the main chain. (There are also a number of polymers such as poly(vinyl acetate) which contain a number of ester groups in side chains but these are not generally considered within the term polyester resins.)... 

Siloxane containing polyester, poly(alkylene oxide) and polystyrene type copolymers have been used to improve the heat resistance, lubricity and flow properties of epoxy resin powder coatings 43). Thermally stable polyester-polysiloxane segmented copolymers have been shown to improve the flow, antifriction properties and scratch resistance of acrylic based auto repair lacquers 408). Organohydroxy-terminated siloxanes are also effective internal mold release agents in polyurethane reaction injection molding processes 409). 

Superior Environmental Products, Inc. introduced a product based on liquid poly sulfide containing 40% of a surface-modified scrap tire mbber. The product, ER-IOOR, is a coating that can temporarily contain chemical, oil, and gasoline spills. Rodriguez [97] reported that an unsaturated polyester resin containing silane-treated CGR showed better mechanical properties than that containing untreated CGR. 

---