Synthesis. A series of latexes was prepared by semicontinuous emulsion polymerization of methyl methacrylate. A dialkyl ester of sodium sulfosuccinic acid surfactant yielded the narrow particle size distribution required. An ammonium persulfate/sodium metabisulfate/ferrous sulfate initiator system was used. The initiator was fed over the polymerization time, allowing better control of the polymerization rate. For the smaller size latexes (200 to 450 nm), a seed latex was prepared in situ by polymerizing 10% of the monomer in the presence of the ammonium persulfate. Particle size was adjusted by varying the level of surfactant during the heel reaction. As the exotherm of this reaction subsided, the monomer and the sodium metabisulfate/ferrous sulfate feeds were started and continued over approximately one hour. The... 

Wu and Zhao studied LIPN systems by a two-stage emulsion polymerization technique (Wu and Zhao 1995). A latex seed (polymer 1) was synthesized first in a semicontinuous emulsion polymerization, swollen by the second-stage monomer or monomer mixture (forming polymer 2), and followed by polymerization to form IPN materials. Six kinds of monomers were used acrylonitrile (AN), vinyl acetate (VAc), n-butyl acrylate (liBA), methyl methacrylate (MMA), ethyl methacrylate (EMA), and ethyl acrylate (EA). The effect of composition, cross-linking level, feeding sequence of polymer 1 and polymer 2 on the IPN miscibility, and... 

The composition and quantity of styrene-maleic anhydride (SMA) copolymer resins were varied in emulsion copolymerisation of methyl methacrylate and n-butyl acrylate conducted by both batch and semicontinuous processes. The resulting particle sizes and levels of coagulum were measured to determine the optimum conditions for incorporation of the SMA resins into the resulting latexes. A semicontinuous process, in which no buffer was included and the SMA was added in a second stage comonomer emulsion, was found to produce coagulum-free latexes. 13 refs. 

Methyl methacrylate-butyl acrylate copolymer latex particles were synthesised by both seeded and unseeded semicontinuous emulsion copolymerisation. Particle size and surface charge densities were characterised by TEM and potentiometric and conductimetric titrations. An investigation of the effect of surface density on zeta-potential is described. 18 refs. 

Aerdts AM, Theelen S JC, Smith TMC, German AL. Grafting of styrene and methyl-methacrylate concurrently onto polybutadiene in semicontinuous emulsion processes and determination of copolymer microstructure. Polymer 1994 35 1648-1653. 

---