Metallic colloidal synthesis

In this chapter, we intend to introduce to the reader some of the most popular preparation methods of noble metal colloids, but do not intend by any means to thoroughly review the scientific literature on metal colloid synthesis. We have chosen examples of synthesis in aqueous and organic solvents, and differentiate between spherical and anisotropic nanoparticles (nanorods and nanoprisms). Additionally, in section 3 we shall describe one of the most popular recent procedures to assemble metal colloids into nanostructured materials (layer-by-layer assembly), as well as the properties of the resulting structures. 

The reduction of transition metal salts in solution is the most widely practiced method for synthesis of metal colloidal suspensions [7]. In the preparation process, polymer is often used in order to prevent the agglomeration of metal particles as well as to control their size. Ahmadi et al. [5] reported that the concentration of the capping polymer affects the shape of platinum particles obtained by salt reduction. This means that the addition of a... 

In the chemical preparation of unprotected metal colloids, the metal concentration usually has a significant influence on the particle size of obtained metal nanoclusters. For example, when increasing Pd concentration from 0.1 to 1.0 mM in the preparation of Pd metal colloids by the thermal decomposition of Pd acetate in methyl isobutyl ketone, the average Pd particle size increased from 8 to 140nm [6,7]. However, in the alkaline EG synthesis method, the size of metal nanoclusters was only slightly dependent on the metal concentration of the colloidal solution. The colloidal Pt particles prepared with a metal concentration of 3.7 g/1 had an average diameter of... 

The approaches used for preparation of inorganic nanomaterials can be divided into two broad categories solution-phase colloidal synthesis and gas-phase synthesis. Metal and semiconductor nanoparticles are usually synthesized via solution-phase colloidal techniques,4,913 whereas high-temperature gas-phase processes like chemical vapor deposition (CVD), pulsed laser deposition (PLD), and vapor transfer are widely used for synthesis of high-quality semiconductor nanowires and carbon nanotubes.6,7 Such division reflects only the current research bias, as promising routes to metallic nanoparticles are also available based on vapor condensation14 and colloidal syntheses of high-quality semiconductor nanowires.15... 

Whichever method is followed, a protective agent able to induce a repulsive force opposed to the van der Waals forces is generally necessary to prevent agglomeration of the formed particles and their coalescence into bulk material. Since aggregation leads to the loss of the properties associated with the colloidal state, stabilization of metallic colloids - and therefore the means to preserve their finely dispersed state - is a cmcial aspect for consideration during their synthesis. 

A promising strategy towards stable and catalyticaUy active metal colloids is their preparation inside the core of micelles formed by amphiphilic block copolymers. This strategy offers a number of advantages (i) micelles represent a nano-structured environment which can be exactly tailored by block copolymer synthesis (ii) polymers act as effective steric stabilizer ]36] (iii) metal leaching might be avoided (iv) micelles allow control over particle size, size distribution and particle solubility [37] and (v) micelles are also supposed to effect catalytic activity and selectivity [38]. 

Barnickel P, Wokaun A (1990) Synthesis of Metal Colloids in Inverse Microemulsions. Mol Phys 69 1-9... 

---