Intrinsic loss shear modulus

With appropriate caUbration the complex characteristic impedance at each resonance frequency can be calculated and related to the complex shear modulus, G, of the solution. Extrapolations to 2ero concentration yield the intrinsic storage and loss moduH [G ] and [G"], respectively, which are molecular properties. In the viscosity range of 0.5-50 mPa-s, the instmment provides valuable experimental data on dilute solutions of random coil (291), branched (292), and rod-like (293) polymers. The upper limit for shearing frequency for the MLR is 800 H2. High frequency (20 to 500 K H2) viscoelastic properties can be measured with another instmment, the high frequency torsional rod apparatus (HFTRA) (294). 

In the case of dynamic mechanical relaxation the Zimm model leads to a specific frequency ( ) dependence of the storage [G ( )] and loss [G"(cd)] part of the intrinsic shear modulus [G ( )] [1]. The smallest relaxation rate l/xz [see Eq. (80)], which determines the position of the log G (oi) and log G"(o>) curves on the logarithmic -scale relates to 2Z(Q), if R3/xz is compared with Q(Q)/Q3. The experimental results from dilute PDMS and PS solutions under -conditions [113,114] fit perfectly to the theoretically predicted line shape of the components of the modulus. In addition l/xz is in complete agreement with the theoretical prediction based on the pre-averaged Oseen tensor. 

Traditionally, tack properties of a PSA have been correlated to their linear rheological behavior, such as elastic and loss modulus [1-3]. While this type of phenomenological analysis provides many clues for the practical design of PSA, it is intrinsically limited by the fact that a tack experiment involves large strains and transient behaviors of the PSA, which cannot be easily predicted by either viscosity (shear, elongational) or any other small strain steady-state dynamical property. The simple observation of the debonding of a PSA tape from a solid... 

---