Phosphate coatings humidity tests

Product Utilization. The principal appHcation for chromium phosphate coatings is as a paint base for painted aluminum extmsions and aluminum beverage can stock. In these appHcations, extremely demanding performance criteria are met by the chromium phosphate conversion coatings. As an example, the Architectural Aluminum Manufacturer s Association Voluntary Specification 605.2-92 requires humidity and salt spray testing for 3000 hours and allows only minimal incidence of paint failure after testing (26). 

The "Mannich" adduct synthesized from the condensation of formaldehyde, 2-(methylamino)ethanol and poly-4-vinylphenol as shown in Structure I, has been evaluated as a function of molecular weight versus corrosion resistance as measured by salt spray and humidity tests on Bonderite 1000, an iron phosphate conversion coating. The molecular weight of the polymer was varied from approximately = 2,900 to 60,000. The corrosion resistance results were essentially equivalent over the molecular weight range evaluated. 

On zinc phosphate conversion coatings, the "Mannich" derivatives of poly-4-vinylphenol have demonstrated performance equivalent to chromic chromate systems in salt spray, humidity, and physical testing. In addition. Table III illustrates results observed with automotive body paint systems evaluated by the "scab" or "cycle" test which causes failure more typical of actual end use conditions than do salt spray evaluations. Again, results equivalent to chromic-chromate post-treatments were obtained. In addition, the humidity resistance and adhesion tests were essentially equivalent to the chromium controls. 

---