Epoxy adhesives Plasticisation

The durability of epoxy-aluminium joints that used a homopolymerised epoxy resin was studied by researchers based in Spain [15], and the effects of relative humidity, temperature, and salt concentration analysed. The homopolymerised epoxy resin absorbed little water (1.5 wt%) because of its non-polar network structure. Increasing relative humidity and temperature enhanced water uptake, but the joint strength remained constant because of epoxy plasticisation. A saline environment was damaging to the adhesive joints because of metal corrosion, but was not significantly harmful to the epoxy resin because of the lower diffusion coefficient of salt water. The decrease in glass transition temperature of the epoxy adhesive due to water absorption was dependent upon only the amount of absorbed water and was independent of hydrothermal ageing conditions. The durability of epoxy adhesive joints made underwater has been studied [16]. 

Epoxies can be modified with various additives, fillers, plasticisers, rubber tougheners and other polymers and so there are a huge number of epoxy adhesives available and numerous specialist grades. 

Aromatic amines formed from the reduction of azo colorants in toy products were analysed by means of HPLC-PDA [703], Drews et al. [704] have applied HPLC/ELSD and UV/VIS detection for quantifying SFE and ASE extracts of butyl stearate finish on various commercial yarns. From the calibrated ELSD response the total extract (finish and polyester trimer) is obtained and from the UV/VIS response the trimer only. Representative SFE-ELSD/UV finish analysis data compare satisfactorily to their corresponding SFE gravimetric weight recovery results. GC, HPLC and SEC are also used for characterisation of low-MW compounds (e.g. curing agents, plasticisers, by-products of curing reactions) in epoxy resin adhesives. 

---