Elastic fracture

In moie ductile materials the assumptions of linear elastic fracture mechanics (LEFM) are not vahd because the material yields more at the crack tip, so that... 

Fracture Mechanics. Linear elastic fracture mechanics (qv) (LEFM) can be appHed only to the propagation and fracture stages of fatigue failure. LEFM is based on a definition of the stress close to a crack tip in terms of a stress intensification factor K, for which the simplest general relationship is... 

Substantial work on the appHcation of fracture mechanics techniques to plastics has occurred siace the 1970s (215—222). This is based on earlier work on inorganic glasses, which showed that failure stress is proportional to the square root of the energy required to create the new surfaces as a crack grows and iaversely with the square root of the crack size (223). For the use of linear elastic fracture mechanics ia plastics, certaia assumptioas must be met (224) (/) the material is linearly elastic (2) the flaws within the material are sharp and (J) plane strain conditions apply ia the crack froat regioa. 

The elastic stress cannot exceed the yield stress of the material, implying a region of local yielding at the crack tip. Nevertheless, to apply the simple framework of hnear elastic fracture mechanics, Irwin [J. Applied Mechanics, 24, 361 (1957)] proposed that this process zone size / be treated as an effective increase in crack length be. Fracture toughness is then given by... 

The importance of inherent flaws as sites of weakness for the nucleation of internal fracture seems almost intuitive. There is no need to dwell on theories of the strength of solids to recognize that material tensile strengths are orders of magnitude below theoretical limits. The Griffith theory of fracture in brittle material (Griflfith, 1920) is now a well-accepted part of linear-elastic fracture mechanics, and these concepts are readily extended to other material response laws. 

Linear Elastic Fracture Mechanics Behavior of Graphite... 

Linear elastic fracture mechanics (LEFM) is based on a mathematical description of the near crack tip stress field developed by Irwin [23]. Consider a crack in an infinite plate with crack length 2a and a remotely applied tensile stress acting perpendicular to the crack plane (mode I). Irwin expressed the near crack tip stress field as a series solution ... 

Although Griffith put forward the original concept of linear elastic fracture mechanics (LEFM), it was Irwin who developed the technique for engineering materials. He examined the equations that had been developed for the stresses in the vicinity of an elliptical crack in a large plate as illustrated in Fig. 2.66. The equations for the elastic stress distribution at the crack tip are as follows. 

Composite materials have many distinctive characteristics reiative to isotropic materials that render application of linear elastic fracture mechanics difficult. The anisotropy and heterogeneity, both from the standpoint of the fibers versus the matrix, and from the standpoint of multiple laminae of different orientations, are the principal problems. The extension to homogeneous anisotropic materials should be straightfor-wrard because none of the basic principles used in fracture mechanics is then changed. Thus, the approximation of composite materials by homogeneous anisotropic materials is often made. Then, stress-intensity factors for anisotropic materials are calculated by use of complex variable mapping techniques. 

The above results are derived from linear elastic fracture mechanics and are strictly valid for ideally brittle materials with the limit of the process zone size going to zero. In order to apply this simple framework of results, Irwin (1957) proposed that the process zone, r be treated as an effective increase in crack length, Sc. With this modification, the fracture toughness becomes... 

Linear combination of atomic orbitals (LCAO) method, 16 736 Linear condensation, in silanol polycondensation, 22 557-558 Linear congruential generator (LCG), 26 1002-1003 Linear copolymers, 7 610t Linear density, 19 742 of fibers, 11 166, 182 Linear dielectrics, 11 91 Linear elastic fracture mechanics (LEFM), 1 509-510 16 184 20 350 Linear ethoxylates, 23 537 Linear ethylene copolymers, 20 179-180 Linear-flow reactor (LFR) polymerization process, 23 394, 395, 396 Linear free energy relationship (LFER) methods, 16 753, 754 Linear higher a-olefins, 20 429 Linear internal olefins (LIOs), 17 724 Linear ion traps, 15 662 Linear kinetics, 9 612 Linear low density polyethylene (LLDPE), 10 596 17 724-725 20 179-211 24 267, 268. See also LLDPE entries a-olefin content in, 20 185-186 analytical and test methods for,... 

ISO 15850 2002 Plastics - Determination of tension-tension fatigue crack propagation -Linear elastic fracture mechanics (LEFM) approach... 

The term fracture toughness or toughness with a symbol, R or Gc, used throughout this chapter refers to the work dissipated in creating new fracture surfaces of a unit nominal cross-sectional area, or the critical potential energy release rate, of a composite specimen with a unit kJ/m. Fracture toughness is also often measured in terms of the critical stress intensity factor, with a unit MPay/m, based on linear elastic fracture mechanics (LEFM) principle. The various micro-failure mechanisms that make up the total specific work of fracture or fracture toughness are discussed in this section. 

---