Curie temperature alloy

The magnetic moments of the heavy RE elements (Gd, Tb, Dy, etc) are coupled antiparallel to the magnetic moments of the TM elements (Fe, Co, etc). The REj TM alloys are therefore ferrimagnetic below their Curie temperature (T )- The heavy TM moments form one magnetic sublattice and the RE moments the other one. In contrast, the light RE moments (eg, Nd, Pr) couple parallel to the moments of TM. The RE spia is always antiparallel to the TM spia, but for the light RE elements, the orbital momentum is coupled antiparallel to the spia and larger than the spia. 

Figure 10 presents the Curie temperature (T ) vs the TM-content (x) for Co- and Fe-based biaary alloys. Alloying rare-earth elements with small amounts of transition metals (x < 0.2) leads to a decrease ia Curie temperature. This is particularly obvious ia the Gd—Co system where it corresponds to a nonmagnetic dilution similar to that of Cu (41,42). This iadicates that TM atoms experience no exchange coupling unless they are surrounded by a minimum number j of other TM atoms. The critical number is j = 5 for Fe and j = 7 for Co. The steep iacrease of for Co-based alloys with x about 0.7 is based on this effect. 

None of the biaary compounds with this composition is well matched to the needs of MO recording. Gd—Fe has too high a Curie temperature and has an in-plane anisotropy. Tp is too low for binary alloys such as Tb—Fe and Dy—Fe. Co-based alloys which exhibit a close to room temperature have... 

Go Binary and Ternary Alloyed Thin Films. Most of the thin-film media for longitudinal and perpendicular recording consist of Co—X—Y binary or ternary alloys. In most cases Co—Cr is used for perpendicular recording while for the high density longitudinal media Co—Cr—X is used X = Pt, Ta, Ni). For the latter it is essential to deposit this alloy on a Cr underlayer in order to obtain the necessary in-plane orientation. A second element combined with Co has important consequences for the Curie temperature (T ) of the alloy, at which the spontaneous magnetisation disappears. The for... 

For alloys of iron, cobalt, nickel, and copper the calculated values of saturation magnetic moments agree closely with the observed values in particular, the maximum value of about 2.48 magnetons at electron number about 26.3 is reproduced by the theory. There is, however, only rough agreement between the observed and calculated values of the Curie temperature. 

An obvious refinement of the simple theory for cobalt and nickel and their alloys can be made which leads to a significant increase in the calculated value of the Curie temperature. The foregoing calculation for nickel, for example, is based upon the assumption that the uncoupled valence electrons spend equal amounts of time on the nickel atoms with / = 1 and the nickel atoms with J = 0. However, the stabilizing interaction of the spins of the valence electrons and the parallel atomic moments would cause an increase in the wave function for the valence electrons in the neighborhood of the atoms with / = 1 and the parallel orientation. This effect also produces a change in the shape of the curve of saturation magnetization as a function of temperature. The details of this refined theory will be published later. 

---