Corrosion inhibitors polarisation curves

The effects of adsorbed inhibitors on the individual electrode reactions of corrosion may be determined from the effects on the anodic and cathodic polarisation curves of the corroding metaP . A displacement of the polarisation curve without a change in the Tafel slope in the presence of the inhibitor indicates that the adsorbed inhibitor acts by blocking active sites so that reaction cannot occur, rather than by affecting the mechanism of the reaction. An increase in the Tafel slope of the polarisation curve due to the inhibitor indicates that the inhibitor acts by affecting the mechanism of the reaction. However, the determination of the Tafel slope will often require the metal to be polarised under conditions of current density and potential which are far removed from those of normal corrosion. This may result in differences in the adsorption and mechanistic effects of inhibitors at polarised metals compared to naturally corroding metals . Thus the interpretation of the effects of inhibitors at the corrosion potential from applied current-potential polarisation curves, as usually measured, may not be conclusive. This difficulty can be overcome in part by the use of rapid polarisation methods . A better procedure is the determination of true polarisation curves near the corrosion potential by simultaneous measurements of applied current, corrosion rate (equivalent to the true anodic current) and potential. However, this method is rather laborious and has been little used. 

Blocking of reaction sites The interaction of adsorbed inhibitors with surface metal atoms may prevent these metal atoms from participating in either the anodic or cathodic reactions of corrosion. This simple blocking effect decreases the number of surface metal atoms at which these reactions can occur, and hence the rates of these reactions, in proportion to the extent of adsorption. The mechanisms of the reactions are not affected and the Tafel slopes of the polarisation curves remain unchanged. Behaviour of this type has been observed for iron in sulphuric acid solutions containing 2,6-dimethyl quinoline, /3-naphthoquinoline , or aliphatic sulphides . 

---