Cobalt catalyst surface area

In the case of cobalt, unstable cubic cobalt was identified as the product of the reduction of standard cobalt catalysts, while hexagonal cobalt was found as a product of the hydrogenation of cobalt carbide. Used cobalt catalysts show no carbide by x-ray examination. Bulk phase carbide decreases the activity of cobalt catalysts. Surface area measurements show no appreciable change when the cobalt of cobalt catalysts was converted to cobalt carbide. Carburization at conditions where free carbon is formed increases the area considerably. 

Bartholomew and coworkers32 described deactivation of cobalt catalysts supported on fumed silica and on silica gel. Rapid deactivation was linked with high conversions, and the activity was not recovered by oxidation and re-reduction of the catalysts, indicating that carbon deposition was not responsible for the loss of activity. Based on characterization of catalysts used in the FTS and steam-treated catalysts and supports the authors propose that the deactivation is due to support sintering in steam (loss of surface area and increased pore diameter) as well as loss of cobalt metal surface area. The mechanism of the latter is suggested to be due to the formation of cobalt silicates or encapsulation of the cobalt metal by the collapsing support. 

Physical Properties of Coked Catalysts. Surface areas for a series of Shell 244 (cobalt-molybdenum (Co-Mo) on alumina) catalysts varying from 0 to 22% coke were determined. The surface area is inversely proportional to coke deposition as shown in Figure 3. The catalysts with 10% coke deposit lose approximately 20% of their original surface areas. 

XPS Analysis. The ultrahigh vacuum (OHV) catalyst treatment-surface analysis system employed to characterize and treat the cobalt catalysts has been described previously ( 1, 2 The catalyst treatment and data analysis procedures have also been described (JJ. Briefly, the samples were treated in quartz reactors and then transferred under UHV into a modified Hewlett-Packard 5950A BSCA spectrometer for emalysis. Peak areas were normalized with theoretical cross-sections (Z) to obtain relative atomic compositions. 

Synthesis of High Surface Area Cobalt-on-Alumina Catalysts by Modification with Organic Compounds... 

The catalysts were characterized by inductively coupled plasma emission spectroscopy (ICP-ES Perkin Elmer Optima 3300RL) to determine cobalt content, x-ray diffraction (XRD Bruker A-500) with crystallite size determination using the Rietveld method, and temperature-programmed reduction (Zeton Altamira AMI-200) using 30 ml/min 10% H2/Ar and a ramp rate of 10°C/min. Surface area... 

The total surface areas determined by the N2 BET method for the calcined, supported catalysts are listed in Table II. The X-ray diffraction (XRD) results showed diffraction peaks from a cubic lattice with a unit cell distance of 6.1 A were present on all of the calcined catalysts. Both C03O4 and C0AI2O4 have structures consistent with that lattice spacing, making assignment of the type of crystalline cobalt species present on the alumina supports difficult. 

A promising bimetallic cathode catalyst for proton exchange fuel cells for the automotive industry is Pt/Co [63], Cobalt is stable as bulk oxide Co304 and can be made with a surface area of about 200 m2/g and has a PZC of about 9 [62],... 

---