Chain polymerization stereochemistry

The orientation of the groups along the carbon chain, its stereochemistry, is critical to the properties of the product. The stereochemistry of addition polymerization can be controlled by the use of catalysts. A polymer where repeating units have the same relative orientation is termed stereoregular. 

The versatility of polymerization resides not only in the different types of polymerization reactions and types of reactants that can be polymerized, but also in variations allowed by step-growth synthesis, copolymerization, and stereospecific polymerization. Chain polymerization is the most important kind of copolymerization process and is considered separately in Chapter 7, while Chapter 9 describes the stereochemistry of polymerization with emphasis on the synthesis of polymers with stereoregular structures by the appropriate choice of polymerization conditions, including the more recent metallocene-based Ziegler-Natta systems. Synthetic approaches to starburst and hyperbranched polymers which promise to open up new applications in the future are considered in an earlier chapter dealing with step-growth polymerization. 

One of the special features of the Ziegler-Natta catalyst is the stereochemistry associated with polymerization. Radical- and cationic-chain polymerization of... 

Anionic living polymerization provides the most important chain polymerization route to block copolymers. By careful control of the reaction conditions it is possible to produce block copolymers with blocks of pre-defined molar mass, narrow molar mass distribution and controlled stereochemistry. In particular, anionic living polymerization is used to prepare block copolymers suitable for use as thermoplastic elastomers (Section 4.5.1), e.g. ABA tri-block copolymers in which homopolymer A is glassy (e.g. polystyrene) and homopolymer B is rubbery (e.g. polyiso-... 

Unlike polyethylene and other simple aikene polymers, natural rubber is a polymer of a diene, isoprene (2-methyl-l,3-butadiene). The polymerization takes place by addition of isoprene monomer units to the growing chain, leading to formation of a polymer that still contains double bonds spaced regularly at four-carbon intervals. As the following structure shows, these double bonds have Z stereochemistry ... 

The configuration of a center in radical polymerization is established in the transition state for addition of the next monomer unit when it is converted to a tetrahedral sp1 center. If the stereochemistry of this center is established at random (Scheme 4.1 km = k,) then a pure atactic chain is formed and the probability of finding a meso dyad, P(m), is 0.5. 

Stereochemistry Coordination Polymerization. Stereoisomerism is possible in the polymerization of alkenes and 1,3-dienes. Polymerization of a monosubstituted ethylene, such as propylene, yields polymers in which every other carbon in the polymer chain is a chiral center. The substituent on each chiral center can have either of two configurations. Two ordered polymer structures are possible — isotactic (XII and syndiotactic (XIII) — where the substituent R groups on... 

The same type of addition—as shown by X-ray analysis—occurs in the cationic polymerization of alkenyl ethers R—CH=CH—OR and of 8-chlorovinyl ethers (395). However, NMR analysis showed the presence of some configurational disorder (396). The stereochemistry of acrylate polymerization, determined by the use of deuterated monomers, was found to be strongly dependent on the reaction environment and, in particular, on the solvation of the growing-chain-catalyst system at both the a and jS carbon atoms (390, 397-399). Non-solvated contact ion pairs such as those existing in the presence of lithium catalysts in toluene at low temperature, are responsible for the formation of threo isotactic sequences from cis monomers and, therefore, involve a trans addition in contrast, solvent separated ion pairs (fluorenyllithium in THF) give rise to a predominantly syndiotactic polymer. Finally, in mixed ether-hydrocarbon solvents where there are probably peripherally solvated ion pairs, a predominantly isotactic polymer with nonconstant stereochemistry in the jS position is obtained. It seems evident fiom this complexity of situations that the micro-tacticity of anionic poly(methyl methacrylate) cannot be interpreted by a simple Bernoulli distribution, as has already been discussed in Sect. III-A. 

The hypothesis of stereochemical control linked to catalyst chirality was recently confirmed by Ewen (410) who used a soluble chiral catalyst of known configuration. Ethylenebis(l-indenyl)titanium dichloride exists in two diaste-reoisomeric forms with (meso, 103) and C2 (104) symmetry, both active as catalysts in the presence of methylalumoxanes and trimethylaluminum. Polymerization was carried out with a mixture of the two isomers in a 44/56 ratio. The polymer consists of two fractions, their formation being ascribed to the two catalysts a pentane-soluble fraction, which is atactic and derives from the meso catalyst, and an insoluble crystalline fraction, obtained from the racemic catalyst, which is isotactic and contains a defect distribution analogous to that observed in conventional polypropylenes obtained with heterogeneous catalysts. The failure of the meso catalyst in controlling the polymer stereochemistry was attributed to its mirror symmetry in its turn, the racemic compound is able to exert an asymmetric induction on the growing chains due to its intrinsic chirality. 

---