Casting double-base

W. G. Clark, Evaluation of 1,2,4-Butanetriol Trinitrate as the EiquidExplosive Plasticiserfor Cast Double Base Propellant Report 4, PTA, Dover, N.J., 1960. [Pg.28]

Tensile Strength of Cast Double-Base Powder as a Function of Nitrocellulose Content P 423 Elongation of Cast Double-Base Powder as a Function of Nitrocellulose. Content. .. P 423 Modulus of Elasticity of Cast Double-Base Powder as a Function of 1 1 ... [Pg.15]

Richardson, Hazards Evaluation of the Cast Double-Base Manufacturing Process , ABL/X- 47 (1960), 45, AD 250858 25) F.A. Warren et... [Pg.629]

Fig 2 Tensile strength of cast double-base powder as function of nitrocellulose content... [Pg.900]

Prediction of the service life of the solid propint third-stage Minuteman motor has been made by Chappell (Ref 48). This motor has a fiberglas case and a cast double-base grain. The motor parameters on which the structural... [Pg.905]

According to Sutton, cast double base charges are likely to contain 45-55% nitrocellulose, 25—40% nitroglycerine, 12-22% plasticiser and 1-2% other ingredients such as stabilisers. Typical properties are ... [Pg.189]

Inhibiting of Cast Double-Base Grains. A good inhibitor should bon.d to the grain with a strength equal to the grain strength itself. [Pg.367]

Inhibiting Double Base Rocket Propellants at Picatinny Arsenal. Most of the work at Pica-tinny Arsn in connection with inhibiting of solventless extruded or cast double-base propellant has been with convolute wrappings of grains or tubes with cellulose acetate. There has been a trend toward use of extruded tubes made by the casting process... [Pg.368]

History. The cast double-base process was developed under U.S. Government auspices during World War II, the initial work being done by Kincaid and Shuey (7). The process filled a need for rocket charges significantly larger than those conveniently made by the then existing extrusion processes. [Pg.10]

Early in the history of the cast double-base process, the principle of screen loading was discovered. In essence, it was found that an evenly... [Pg.22]

The dilatometric behavior of cast double-base propellant reveals much concerning the nature of the cure process. As an illustrative example, Figure 19 shows the curing behavior at constant temperature, 80°F., for a casting powder which has a porosity of about 2.7% based on the total propellant volume. [Pg.33]

During the past 10 years great strides have been made in the development and service application of highly loaded, synthetic rubber-base and interstitially-cast double-base composite-modified propellants. Largely for this reason and for economic and logistic reasons as well, the slurry-cast nitrocellulose plastisols have been relegated to a secondary role. [Pg.39]

Nonpolymerizable, castable, gel-type (cast double base powder) ... [Pg.365]

The composition of various more modern cast double base propellants (according to Sutton [56] and J. Taylor [57] is shown in Table 194. Table 195 gives the physico-chemical properties of propellant I. [Pg.675]

ANB. Code name for a cast double-base propellant described in classified "Propellant Manual SPIA/M2, JohnsHopkinsUniv, SilverSpring,Md(l959), Unit No 407... [Pg.401]

Refs l)Beil 26, 396 2)W.Lessen J. Colman, Ann 298, 115(1897) Dinitroanisyltetrazole, CgH NgOg —not found in Beil or CA through 1956 Trinitroanisyltetfazole, C,HS N707 — not found in Beil or CA through 1956 ANJ. Cast double-base propellant described in conf "Propellant Manual, SP IA/M2( 1959),... [Pg.457]

ANU. A cast double-base propellant described in conf Propellant Manual SPIA/MZ(1959) Unit No 412... [Pg.473]

A0E A0K A0R AOV. Cast double-base propellants described in conf "Propellant Manual," SPIA/M2(1959),UnitNos414,415,416 4l7... [Pg.473]