Calcium-oxide

Calcium oxide (calx, quicklime) is hydrated to calcium hydroxide, which is reacted with carbon dioxide to produce precipitated calcium carbonate (filler). 

Calcium oxide is used as a flux in steel production and in building and construction materials. Calcium oxide is also important in paper manufacture, sewage treatment, agriculture, leather tanning, and glass manufacturing. 

---

Heavy metals often can be removed effectively by chemical precipitation in the form of carbonates, hydroxides, or sulfides. Sodium carbonate, sodium bisulfite, sodium hydroxide, and calcium oxide are all used as precipitation agents. The solids precipitate as a floe containing a large amount of water in the structure. The precipitated solids need to be separated by thickening or filtration and recycled if possible. If recycling is not possible, then the solids are usually disposed of to a landfill. 

Some carbonates are important industrial chemicals. Calcium carbonate occurs naturally in several forms, including limestone, and is used in the production of quicklime, calcium oxide CaO, slaked (or hydrated) lime, calcium hydroxide Ca(OH)2 and cement. 

The calcium oxide so produced is slaked to give a suspension of calcium hydroxide and this is heated with the filtrate from the carbonator which contains ammonium chloride ... 

After drying over quicklime, calcium oxide CaO, the ammonia is collected by upward delivery. (N.B. Both of the common drying agents, calcium chloride and concentrated sulphuric acid, combine with the gas.)... 

The gases from the kiln contain about 9% sulphur dioxide. (The calcium oxide combines with the silica to form a silicate slag which, when cool, is crushed and mixed with some anhydrite to give cement, a valuable by-product.)... 

Reaction (13.4) is exothermic and reversible, and begins at about 700 K by Le Chatelier s Principle, more iron is produced higher up the furnace (cooler) than below (hotter). In the hotter region (around 900 K), reaction (13.5) occurs irreversibly, and the iron(II) oxide formed is reduced by the coke [reaction (13.6)] further down. The limestone forms calcium oxide which fuses with earthy material in the ore to give a slag of calcium silicate this floats on the molten iron (which falls to the bottom of the furnace) and can bo run off at intervals. The iron is run off and solidified as pigs —boat-shaped pieces about 40 cm long. 

It occurs chiefly as cinnabar, the red sulphide HgS, from which it is readily extracted either by roasting (to give the metal and sulphur dioxide) or by heating with calcium oxide the metal distils off and can be purified by vacuum distillation. 

Laughing gas, see Nitrogen(I) oxide Lautarite, see Calcium iodate Lawrencite, see Iron(II) chloride Lechatelierite, see Silicon dioxide Lime, see Calcium oxide Litharge, see Lead(II) oxide... 

The calcium oxide product is supplemented with fresh limestone and returned to the fluidized bed. Two undesirable side reactions can occur in the regeneration of spent lime leading to the production of calcium sulfide ... 

The polymerization is carried out at temperatures of 0—80°C in 1—5 h at a soHds concentration of 6—12%. The polymerization is terminated by neutralizing agents such as calcium hydroxide, calcium oxide, calcium carbonate, or lithium hydroxide. Inherent viscosities of 2-4 dL/g are obtained at 3,4 -dianiinodiphenyl ether contents of 35—50 mol %. Because of the introduction of nonlinearity into the PPT chain by the inclusion of 3,4 -dianiinodiphenyl ether kinks, the copolymer shows improved tractabiUty and may be wet or dry jet-wet spun from the polymerization solvent. The fibers are best coagulated in an aqueous equiUbrium bath containing less than 50 vol % of polymerization solvent and from 35 to 50% of calcium chloride or magnesium chloride. 

Calcium hydride is highly ionic and is insoluble in all common inert solvents. It can be handled in dry air at low temperatures without difficulty. When heated to about 500°C, it reacts with air to form both calcium oxide and nitride. Calcium hydride reacts vigorously with water in either Hquid or vapor states at room temperature. The reaction with water provides 1.06 Hters of hydrogen per gram CaH2. 

The calcium oxide is leached out with acid (HCl), leaving a finely divided T1H2 powder. 

In the vapor phase, acetone vapor is passed over a catalyst bed of magnesium aluminate (206), 2iac oxide—bismuth oxide (207), calcium oxide (208), lithium or 2iac-doped mixed magnesia—alumina (209), calcium on alumina (210), or basic mixed-metal oxide catalysts (211—214). Temperatures ranging... 

Thermal Properties. Because all limestone is converted to an oxide before fusion or melting occurs, the only melting point appHcable is that of quicklime. These values are 2570°C for CaO and 2800°C for MgO. Boiling point values for CaO are 2850°C and for MgO 3600°C. The mean specific heats for limestones and limes gradually ascend as temperatures increase from 0 to 1000°C. The ranges are as follows high calcium limestone, 0.19—0.26 dolomitic quicklime, 0.19—0.294 dolomitic limestone, 0.206—0.264 magnesium oxide, 0.199—0.303 and calcium oxide, 0.175—0.286. 

Drying a.nd Calcination. The simplest pyrometaHurgical operation is the evaporation of free water and the decomposition of hydrates and carbonates. A typical reaction is the decomposition of pure limestone [1317-65-3] CaCO, to calcium oxide [1305-78-8] and carbon dioxide ... 

Calcium Peroxide. Pure calcium peroxide [1305-79-9] Ca02, has been prepared, but the commercial product is a mixture made by reaction of calcium hydroxide and hydrogen peroxide. Commercial material contains either 60 or 75% Ca02 the remainder is a poorly defined mixture of calcium oxide, hydroxide, and carbonate. A well-defined octahydrate [60762-59-6] 8H20, can be crysta11i2ed from aqueous systems. 

---