Alloying elements, effect chromium

The important (3-stabilizing alloying elements are the bcc elements vanadium, molybdenum, tantalum, and niobium of the P-isomorphous type and manganese, iron, chromium, cobalt, nickel, copper, and siUcon of the P-eutectoid type. The P eutectoid elements, arranged in order of increasing tendency to form compounds, are shown in Table 7. The elements copper, siUcon, nickel, and cobalt are termed active eutectoid formers because of a rapid decomposition of P to a and a compound. The other elements in Table 7 are sluggish in their eutectoid reactions and thus it is possible to avoid compound formation by careful control of heat treatment and composition. The relative P-stabilizing effects of these elements can be expressed in the form of a molybdenum equivalency. Mo (29) ... 

Mechanical properties depend on the alloying elements. Addition of carbon to the cobalt base metal is the most effective. The carbon forms various carbide phases with the cobalt and the other alloying elements (see Carbides). The presence of carbide particles is controlled in part by such alloying elements such as chromium, nickel, titanium, manganese, tungsten, and molybdenum that are added during melting. The distribution of the carbide particles is controlled by heat treatment of the solidified alloy. 

Chromium is the most effective alloying element for promoting resistance to oxidation. Table 3.10 gives temperatures at which steels can be used in air without excessive oxidation. In atmospheres contaminated with sulfur, lower maximum temperatures are necessary. 

Tomashov, N. D., Chernova, G. P. and Markova, O. N., Effect of Alloying Elements on the Tendency of Stainless Chromium-Nickel Steels to Pitting Corrosion , Sa. Korroziya Meta i Splavov, 73 (1963) C.A., 60, 3805b... 

The corrosion behaviour of amorphous alloys has received particular attention since the extraordinarily high corrosion resistance of amorphous iron-chromium-metalloid alloys was reported. The majority of amorphous ferrous alloys contain large amounts of metalloids. The corrosion rate of amorphous iron-metalloid alloys decreases with the addition of most second metallic elements such as titanium, zirconium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, cobalt, nickel, copper, ruthenium, rhodium, palladium, iridium and platinum . The addition of chromium is particularly effective. For instance amorphous Fe-8Cr-13P-7C alloy passivates spontaneously even in 2 N HCl at ambient temperature ". (The number denoting the concentration of an alloy element in the amorphous alloy formulae is the atomic percent unless otherwise stated.)... 

Chromium is the most effective alloying element to give resistance to oxidation, forming a tenacious oxide film. Chromium alloys should be specified for equipment subject to temperatures above 500°C in oxidising atmospheres. 

The anodic polarization of a given alloy base metal such as iron or nickel is sensitive to alloying element additions and to heat treatments if the latter influences the homogeneity of solid solutions or the kinds and distribution of phases in the alloy. The effect of chromium in iron or nickel is to decrease both EpP and icrit and hence to enhance the ease of placing the alloy in the passive state. The addition of chromium to iron is the basis for a large number of alloys broadly called stainless steels, and chromium additions to nickel lead to a series of alloys with important corrosion-resistant properties. 

The major alloying element contributing to resistance to pitting corrosion in iron- and nickel-base alloys is chromium. The effect of chromium in reducing both the critical current density and the passivating potential of iron in 1 N H2S04 is shown by the polarization curves of... 

---