Zinc oxide defect structure

One feature of oxides is drat, like all substances, they contain point defects which are most usually found on the cation lattice as interstitial ions, vacancies or ions with a higher charge than dre bulk of the cations, refened to as positive holes because their effect of oxygen partial pressure on dre electrical conductivity is dre opposite of that on free electron conductivity. The interstitial ions are usually considered to have a lower valency than the normal lattice ions, e.g. Zn+ interstitial ions in the zinc oxide ZnO structure. 

Zinc oxide is normally an w-type semiconductor with a narrow stoichiometry range. For many years it was believed that this electronic behavior was due to the presence of Zn (Zn+) interstitials, but it is now apparent that the defect structure of this simple oxide is more complicated. The main point defects that can be considered to exist are vacancies, V0 and VZn, interstitials, Oj and Zn, and antisite defects, 0Zn and Zno-Each of these can show various charge states and can occupy several different... 

The defect structure of zinc oxide involves interstihal zinc ions and excess or quasi-free electrons according to Equahons (3.1) and (3.2) ... 

As indicated in Table 10.18, a zinc-rich primer is often recommended. It can be an organic zinc-epoxy or an inorganic zinc-ethyl-silicate primer. Zinc-rich primers are also used as so-called shop primers, or prefabrication primers, for temporary protection of semi-manufactured steel goods. After fabrication, e.g. of welded steel structures, the shop primer surface must be cleaned (degreased), and possible shop primer defects and weld joints have to be blast cleaned and coated with a primer before the whole structure is painted. Iron oxide is also used as a pigment in some shop primers. These must not be overpainted with a zinc-rich paint. 

---