Trans-vinylene groups polybutadiene

The first-order rate constants for terminal vinyl groups and for trans-vinylene groups in linear polyethylene were observed by Dole and Williams (8) to be 20 to 30 times higher than our corresponding rates in the amorphous trans- and vinyl polybutadienes (Table III). On the other hand, the initial yields were lower than our G0 values because of the... 

To determine the concentration of cis-vinylene groups in irradiated specimens, the original cw-polybutadiene itself was used as a standard, and a value for A (assumed independent of concentration) was determined from Av and logr (I0/I)vo of unirradiated specimens. The total concentration of unsaturation was accepted (15) as 100% of theoretical and the density as 0.90 gram per cc. The cis concentration was obtained by subtracting from the total unsaturation the trans-vinylene and vinyl contents determined from the calibration curves developed as described below. The value of A so determined was 2.67 X 103 liters/mole-sq. cm. 

The data of Table II indicate that the etch rates for CB and its "homologues"—TP, CO (or TO), and EPM—tend to increase monotonically with a decrease in vinylene (-CH=CH-) unsaturation. The elastomeric EPM was chosen instead of crystalline polyethylene as a model for the fully saturated CB to avoid a morphology factor in etch rates, as was observed with crystalline TB. The difference in etch rates for the partially crystalline TO and the elastomeric CO (ratio of about 1.2 1.0) is attributable more to a morphology difference between these polyoctenamers than to the difference in their cis/trans content. Cis/trans content had likewise no perceptible effect on etch rates in the vinyl-containing polybutadienes (see Table I) if there was a small effect, it was certainly masked by the dominant effect of the vinyl groups. 

To obtain the absorbances at 910 and 967 cm. 1, it was necessary to correct the observed band intensities for the overlapping of adjacent bands. The band at 910 cm."1 for the vinyl group was corrected for the absorbance from the wing of the 967-cm."1 frarw-vinylene band,. and the latter band was corrected for the vinyl band at 995 cm. 1. The Lorentz band shape equation was used to calculate the absorbance in the wings, and in the thicker specimens, successive approximations were necessary. This treatment gave the four equations below, which yielded the concentrations of trans and vinyl groups for the emulsion and sodium polybutadienes listed in Table I. Implicit in these equations is the assumption that the absorptivities are independent of concentration. 

---