Toughened acrylics cure mechanism

The second means of transforming a liquid adhesive entirely into a solid without the loss of a solvent or dispersion medium is to produce solidification by a chemical change rather than a physical one. Such reactive adhesives may be single-part materials that generally require heating or exposure to electron beam or UV or visible radiation (see Radiation-cured adhesives) to perform the reaction, and which may be solids (that must be melted before application), liquids or pastes. The alternative two-part systems require the reactants to be stored separately and mixed only shortly before application. The former class is exemplified by the fusible, but ultimately reactive, epoxide film adhesives and the latter by the two-pack Epoxide adhesives and Polyurethane adhesives and by the Toughened acrylic adhesives that cure by a free-radical Chain polymerization mechanism. 

In recent years, the range of adhesive materials used in automotive manufacture has expanded to include polyurethanes, plastisols, phenolics, hot melts, anaerobics, cyanoacrylates, toughened acrylics and epoxies (see Structural and Hot melt adhesives). Selection criteria are based principally upon the nature of the adherends, the mechanical properties required under service conditions and application and curing characteristics. 

Studies of the particle—epoxy interface and particle composition have been helphil in understanding the mbber-particle formation in epoxy resins (306). Based on extensive dynamic mechanical studies of epoxy resin cure, a mechanism was proposed for the development of a heterophase morphology in mbber-modifted epoxy resins (307). Other functionalized mbbers, such as amine-terminated butadiene—acrylonitrile copolymers (308) and -butyl acrylate—acryhc acid copolymers (309), have been used for toughening epoxy resins. 

---