Tellurium Polycrystalline Film

Darkowski and Cocivera [94] investigated trialkyl- or triarylphosphine tellurides, as low-valent tellurium sources, soluble in organic solvents. They reported the cathodic electrodeposition of thin film CdTe on titanium from a propylene carbonate solution of tri-n-butylphosphine telluride and Cd(II) salt, at about 100 °C. Amorphous, smooth gray films were obtained with thicknesses up to 5.4 p,m. The Te/Cd atomic ratio was seen to depend on applied potential and solution composition with values ranging between 0.63 and 1.1. Polycrystalline, cubic CdTe was obtained upon annealing at 400 C. The as-deposited films could be either p- or n-type, and heat treatment converts p to n (type conversion cf. Sect. 3.3.2). 

The UPD and anodic oxidation of Pb monolayers on tellurium was investigated also in acidic aqueous solutions of Pb(II) cations and various concentrations of halides (iodide, bromide, and chloride) [103]. The Te substrate was a 0.5 xm film electrodeposited in a previous step on polycrystalline Au from an acidic Te02 solution. Particular information on the time-frequency-potential variance of the electrochemical process was obtained by potentiodynamic electrochemical impedance spectroscopy (PDEIS), as it was difficult to apply stationary techniques for accurate characterization, due to a tendency to chemical interaction between the Pb adatoms and the substrate on a time scale of minutes. The impedance... 

---