Self-Assembly, X-ray, and Electrical Conductivity in HT-PATs

The self-assembly structure leads to a large increase in electrical condutivity in HT-PATs relative to irregular PATs. While the measured conductivity of HT-PAT 

1000 5/cm Rigior g. HT-PDDT as cast. Typical values range from 100-500 S/cm 

McCullough [62, 67] exhibited maximum electrical conductivities of 200 S cm for POT and 150 S cm for PHT [76]. McCullough et al. have routinely measured conductivities of 100-200 S cm in these samples in HT-PDDT [78] (Fig. 2). In contrast, PDDT from FeCl3 generally gave conductivities of 0.1-1 S cm (58-70% HT). Rieke and co-workers have also reported that the electrical conductivities for their HT-PATs have conductivities of 1000 S cm conductivity for HT-PBT is 1350 S cm 

---