Polyphosphazenes Mechanical properties

Hydrodynamic and optical properties of polymers [NP(OR)2]n [R = CH2CF3, CH2(CF2)2H, CH2(CF2)4H] have been analysed. Mechanical properties of polyphosphazene-silicate nanocomposites, prepared from (NP[(0CH2CH2)20Me]2 n (MEEP) and tetraethoxysilane, have been investigated as function of the catalyst used. ... 

Although the poor mechanical properties limit their applications to repair load-bearing defects, the inherited buffering capacity of polyphosphazenes to neutralize the acidic degradation of PLA makes this a unique system. 

Sulfonated aromatic polymers have been widely studied as alternatives to Nafion due to potentially attractive mechanical properties, thermal and chemical stability, and commercial availability of the base aromatic polymers. Aromatic polymers studied in fuel cell apphcations include sulfonated poly(p-phenylene)s, sulfonated polysulfones, sulfonated poly(ether ether ke-tone)s (SPEEKs), sulfonated polyimides (SPIs), sulfonated polyphosphazenes, and sulfonated polybenzimidazoles. Representative chemical structures of sulfonated aromatic polymers are shown in Scheme 3. Aromatic polymers are readily sulfonated using concentrated sulfuric acid, fuming sulfuric acid, chlorosulfonic acid, or sulfur trioxide. Post-sulfonation reactions suffer from a lack of control over the degree and location of functionalization, and the... 

Poiyphosphazene Biends Blends of sulfonated polyphosphazene, for example, sulfonated poly[bis(3-methylphenoxy)phosphazene] or poly[(bisphenoxy)phosphazene] (see Fig. 29.14) with either an inert organic polymer such as poly(vinylidene fluoride) (Pintauro and Wycisk, 2004 Wycisk et al., 2002) or polyacrylonitrile (Carter et al., 2002) or a reactive polymer (e.g., polybenzimidazole) (Wycisk et al., 2005) have been investigated. The resultant membranes had conductivities of 0.01-0.06 S/cm (in water at 25°C) and equilibrium water swelling from 20 to 60% (at 25°C). Blends of poly[(bisphe-noxy)phosphazene] and polybenzimidazole (where acid-base complexation occurred between the sulfonic acid and the imidazole nitrogen) exhibited good mechanical properties and low methanol permeability. MEAs with this membrane material outperformed Nafion 117 in a DMFC at 60°C with concentrated (5-10 M) methanol feeds. With 1.0 M methanol and 0.5 L/min ambient air at 60°C, the maximum power density was 97 mW/cm and the methanol crossover was 2.5 times lower than that with Nafion 117 (Wycisk et al., 2005). 

Aryloxyphosphazene copolymers can also confer fireproof properties to flammable materials when blended. Dieck [591] have used the copolymers III, and IV containing small amounts of reactive unsaturated groups to prepare blends with compatible organic polymers crosslinkable by the same mechanism which crosslinks the polyphosphazene, e.g. ethylene-propylene and butadiene-acrylonitrile copolymers, poly(vinyl chloride), unsaturated urethane rubber. These blends were used to prepare foams exhibiting excellent fire retardance and producing low smoke levels or no smoke when heated in an open flame. Oxygen index values of 27-56 were obtained. 

---