Polymer nanocomposites polyester resin/clay

M. H. Beheshty, M. Vafayan, and M. Poorabdollah. Low profile unsaturated polyester resin-clay nanocomposite properties. Polymer Compositer, 305 (2009), 629 38. 

Incorporation of modified clays into thermosetting resins, and particularly in epoxy35 or unsaturated polyester resins, in order to improve thermal stability or flame retardancy, has been reported.36 A thermogravimetric study of polyester-clay nanocomposites has shown that addition of nanoclays lowers the decomposition temperature and thermal stability of a standard resin up to 600°C. But, above this temperature, the trend is reversed in a region where a charring residue is formed. Char formation seems not as important as compared with other polymer-clay nanocomposite structures. Nazare et al.37 have studied the combination of APP and ammonium-modified MMT (Cloisite 10A, 15A, 25A, and 30B). The diluent used for polyester resin was methyl methacrylate (MMA). The... 

The procedure to obtain nanocomposites based on unsaturated polyester resins leads to improvements in the order of 120% in the flexural modulus, 14% in flexural strength and 57% increase in tensile modulus with 4.7% of clay slurry content. Thermal stability augments and the gelation temperature increases to 45 °C, as compared to that of the resin (Fig. 31.6). It seems that adding water to the MMT allows better intercalation of polymer chains into the interlamellar space. Because clay is first suspended in water, this improves dispersion and distribution of the particles in the resin matrix. Longer gelation times lead to more uniform and mechanically stronger structures and to yield stresses (Fig. 31.7). Enhanced polymer-clay interactions are revealed by XPS in this case (Fig. 31.8). 

---