Poly polythiophene blends, formation

The inclusion of 5 wt% PCBM [l-(3-methoxycarbonyl)propyl-l-phe-nyl-[6,6]C6i] in the spin-coating solutions resulted in efficient polymer emission quenching for all the polythiophenes studied. The transient absorption spectra of the amorphous poly(541)/PCBM blend film. At 10 ps exhibited an absorption peak around 700 nm, similar to that observed for the poly(541) pristine film. The shape of the transient spectrum varied with time, with the absorption peak shifting from 700 nm at 10 is to 900 nm for time delays >100 (is, demonstrating the formation of two distinct transient species in the blend film. The monoexponential lifetime was t = 8 (is under Ar atmosphere and significantly shortened under 02 atmosphere. Monoexponential phase is therefore assigned to the decay of poly(541) triplet excitons. 

Poly (thiophene)s are of particular interest as electfochromic materials owing to their chemical stability, ease of synthesis and processability. For the most part, current research has been focused on composites, blends and copolymer formations of several conjugated polyheterocyclics, polythiophene and its derivatives, especially PEIX)T. In one example, poly(3,4-ethylenedioxythiophene) (PEDOT)/poly(2-acrylamido-2-methyl-l-propanesulfonate) (PAMPS) composite films were prepared by Sonmez et al. for alternative electrochromic applications [50]. Thin composite films comprised of PEDOT/PAMPS were reported to switch rapidly between oxidized and neufial states, in less than 0.4 s, with an initial optical contrast of 76% at A.max. 615 nm. Nanostructured blends of electrochromic polymers such as polypyrrole and poly(3,4-ethylenedioxythiophene) were developed via self-assembly by Inganas etal. for application as an electrochromic window [26]. Uniir etal. developed a graft-type electrochromic copolymer of polythiophene and polytetrahydrofuran for use in elecfiochromic devices [51]. Two EDOT-based copolymers, poly[(3,4-ethylenedioxythiophene)-aZ/-(2,5-dioctyloxyphenylene)] and poly[(3,4-ethylenedioxythiophene)-aft-(9,9 -dioctylfluorene)] were developed by Aubert et al. as other candidates for electrochromic device development [52],... 

---