Hydroxyl-functionalized polymers using group after polymerization

Achiral polymers synthesized from achiral monomers have been modified after polymerization using asymmetric catalysts to yield optically active polymers. For example, enantioselective ketone reduction, hydrogenation, olefin epoxida-tion, and olefin hydroxylation have been carried on the functional groups of achiral polymers [111, 112]. Such functionalizations, however, are often incomplete or occur with a low degree of asymmetric control. 

Polymeric supports can also be used with advantage to form monofunctional moieties from difunctional (Hies. Leznoff has used this principal in the synthesis of sex attractants on polymer supports (67). Starting from a sheap symmetrical diol he blocked one hydroxyl group by the polymer. Functionalization of cross-linked polymers is mostly performed by chloromethylation (65). A very promising method to introduce functional groups into crosslinked styrene-divinylbenzene copolymers is the direct lithiation with butyllithium in presence of N,N,N, N -tetramethyl-ethylenediamine (TMEDA) (69, 70). Metalation of linear polystyrene with butyl-lithium/TMEDA showed no exchange of benzylic hydrogen and a ratio of attack at m/p-position of 2 1 (71). In the model reaction of cumene with amylsodium, a kinetic control of the reaction path is established. After 3h of treatment with amyl-sodiuni, cumene is metalated 42% in a-, 39% m-, and 19% p-position. After 20h the mixture equilibrates to affort 100% of the thermodynamically more stable a-prod-uct (72). 

In the second method, the alkoxyamine-ftmctionalized backbone is prepared by a chemical modification of a preformed polymer. Abbasian and Entezami prepared alkoxyamine-functionalized poly(vinyl chloride) (PVC) in a three-step procedure. PVC was first arylated with toluene by Friedel-Crafts acylation followed by a bromination step using N-bromosuccinimide. The bromine atom was finally reacted via nucleophilic substitution by the TEMPO hydro-xylamine anion. PVC-g-PS was finally obtained after TEMPO-mediated polymerization of styrene. A TEMPO-functionalized isotactic poly(l-butene) macroinitiator was synthesized by Jo et al. who used a rhodium-catalyzed activation of the alkane C-H bonds and subsequent transformations of the boronate ester group into an hydroxyl pendant group. This reactive moiety was then used to attach a TEMPO-based alkoxyamine bearing another hydroxy function by an ether linkage. A method to prepare PE-g-PS from a poly(ethylene-co-m,p--methylstyrene) obtained by metallocene-catalyzed polymerization was also reported. The macroalkoxya-mine was synthesized after bromination with N-bromosuccinimide followed by a nucleophilic reaction with the TEMPO hydroxylamine anion. 

---