Creep compliance parameters extracted

Table 14.1 Characteristics M, M /Mn and Tg (based on DSC and defined at ts = 1,000sec) and parameters A, / and Z extracted by analyzing the creep-compliance J(t) curves or viscoelastic spectra G (ta) of the polystyrene samples, whose structural-relaxation times TS, structural-growth parameters s and frictional factors K are displayed, respectively, in Figs. 14.13, 14.14 and 14.15. Also shown are the K values at 127.5°C of samples A, B, C and F2 along with the average value of K shown in Table 10.1 and the Mw, MwjMn, and Tg (DCS) of F2. The reference theory used in each analysis is indicated. 

Special specimen preparation as with tensile testing. However, the extraction of intrinsic mechanical parameters from creep indentation data is analytically complex [3, 4]. Confined compression or unconfined compression tests require preparation of cylindrical cored specimens of tissue and underlying bone. With unconfined compression, the free draining tissue edges and low aspect ratio, layered nature of the test specimen may introduce error. Compression of a laterally confined specimen by a porous plunger produces uniaxial deformation and fluid flow. Confined compression creep data has been analyzed to yield an aggregate equilibrium compressive modulus and permeability coefficient [5] and uniaxial creep compliance [6]. 

A and D indicate the two parameters most commonly extracted from a creep curve. A represents the instantaneous elastic compliance and can be used to calculate an elastic modulus. D represents the limiting viscosity, which is related to the reciprocal of the slope. In some cases, parameters from creep testing have been related to molecular mechanisms (Shama and Sherman, 1970 Davis, 1973 deMan et al., 1985). The parameters have also been correlated with hardness and spreadability (Scott-Blair, 1938). 

---

See also in sourсe #XX -- [ , , , ]

---