Because of their lower level of crystallinity these copolymeis soften at lower temperatures than polyethylene. Table I compares the torsional stiffness at various temperatures of an 18% ethyl acrylate-82 % ethylene copolymer with that of a 21,000 molecular weight, 0.918 density polyethylene made by high pressure polymerization (Bakelite DYNH, Union Carbide Corp.). 

The effect of the components and conditions of preparation on the properties of a 70/30 LDPE/clay composite is shown in Table I. The 10/90 mixture of LDEE Bakelite Polyethylene Resin DYNH-1 (Union Carbide Corp.) and Hydrite 10 clay (Georgia Kaolin Co.) was compounded at 150 C in the Brabender Plasticorder in the presence of MAH and/or t-butyl perbenzoate (tBPB). The EE-coated clay was then mixed with additional DYNH-1 LDPE at 130°C to yield a 70/30 PE/clay composite. A 30 70 PE/clay concentrate was prepared in a similar manner at 150 C and converted to a 70/30 EE/ clay composite at 130 C. The 10/90 PE/clay concentrate is an easily handled, clay-like product while the 30/70 concentrate is... 

---