Suberized Cell Walls. An analogous set of CPMAS experiments is presented for suberin in Figure 6. Because this polymer is an integral part of the plant cell wall, the 13C NMR spectrum had contributions from both polysaccharide and polyester components. Chemical-shift assignments, summarized in Table IV, demonstrated the feasibility of identifying major polyester and sugar moieties despite serious spectral overlap. Semiquantitative estimates for the various carbon types indicated that, as compared with cutin, the suberin polyester had dramatically fewer aliphatic and more aromatic residues. A similar observation was made previously for the soluble depolymerization products of these plant polymers (1,8,11). 

Solid-state 13C NMR was employed to characterize intact samples of cutin and suberin biopolyesters. Although a considerable degree of structural heterogeneity was observed for both materials, it was possible nonetheless to resolve and assign many NMR peaks, even when the polyesters were accompanied by waxes or cell walls. Quantitative estimates for the various aliphatic, aromatic, and carbonyl carbon types indicated that cutin was primarily aliphatic in composition, whereas suberin had more aromatic and olefinic moieties. Additional analysis should be facilitated by the biosynthetic incorporation of selectively 13C-enriched precursors (26,27). 

These results demonstrated the usefulness of 13C NMR in studies of molecular structure and dynamics for the polymeric constituents of plant cuticle. Although these materials are insoluble and sometimes present as interpenetrating phases, CPMAS and spin relaxation techniques helped identify important carbon types and provided structural clues to the protective functions of cutin and suberin in terrestrial plants. 

---