Steam generation accelerated tests

Coal ash corrosion is a widespread problem for superheater and reheater tubes in coal fired power plants that bum high-sulfur coals. The accelerated corrosion is caused by liquid sulfates on the surface of the metal beneath an over-lying ash deposit. Coal ash corrosion is very severe between 540 and 740°C (1000°F and 1364°F) because of the formation of molten alkali iron-trisulfate. Considerable work has been done to predict corrosion rates based on the nature of the coal (its sulfur and ash content). This was accomplished by the exposure of various alloys to synthetic ash mixtures and synthetic flue gases. The corrosion rates of various alloys were repotted in the form of iso-corrosion curves for various sulfur dioxide, alkali sulfiite, and temperature combinations. An equation was developed to predict corrosion rates for selected alloys from details of the nature of ash by analyzing deposits removed from steam generator tubes and from test probes installed in a boiler [33]. Then laboratory tests were conducted using coupons of various tdloys coated with synthetic coal ash that was exposed to simulated combustion gas atmospheres. 

---