Polymers single-cantilever clamps

DMT A measurements were made with a Polymer Labs instrument. Samples were clamped in the single cantilever mode in a frame of 22 mm using 6 mm clamps with 0.5 mm faces. The sample length between the clamps was 8 mm. Measurements were performed at a frequency of 1 Hz, a strain amplitude of 0.063 mm and a heating rate of 5 K.min . Clamping was checked by monitoring the strain amplitude on an oscilloscope. The measurements were carried out in air. Values of the temperature of maximum mechanical loss, T (tan 5max). were reproducible to 2 K. 

BENDING OF A BEAM. The complex dynamic Young s modulus can be determined from the forced, non-resonant oscillations of a single or double cantilever beam. The apparatus considered in this paper is the Dynamic Mechanical Thermal Analyzer (DMTA) (6), manufactured by Polymer Laboratories, Inc. Figure 3 shows the experimental setup for the single cantilever measurement. A thin sample is clamped at both ends. One end is attached to a calibrated shaker through a drive shaft. 

---