Phenylenes relative energies

The PL spectrum and onset of the absorption spectrum of poly(2,5-dioctyloxy-para-phenylene vinylene) (DOO-PPV) are shown in Figure 7-8b. The PL spectrum exhibits several phonon replica at 1.8, 1.98, and 2.15 eV. The PL spectrum is not corrected for the system spectral response or self-absorption. These corrections would affect the relative intensities of the peaks, but not their positions. The highest energy peak is taken as the zero-phonon (0-0) transition and the two lower peaks correspond to one- and two-phonon transitions (1-0 and 2-0, respectively). The 2-0 transition is significantly broader than the 0-0 transition. This could be explained by the existence of several unresolved phonon modes which couple to electronic transitions. In this section we concentrate on films and dilute solutions of DOO-PPV, though similar measurements have been carried out on MEH-PPV [23]. Fresh DOO-PPV thin films were cast from chloroform solutions of 5% molar concentration onto quartz substrates the films were kept under constant vacuum. 

Aromatic polyesters were particularly good candidates for this new field of thermotropic main-chain polymers, since the relatively low energy of association of the ester groups led to low inter-chain forces. Further research led to the discovery that incorporation of 2,6-naphthylene or of 4,4 -biphenylyl groups, in addition to p-phenylene groups, as components of aromatic polyesters, introduced a useful new degree of randomness. Particularly useful, and the basis of the commercial products Vectra (polymer) and Vectran (fibre) from Hoechst-Celanese and Kuraray, are the copolymers formed by polymerisation of mixtures of p-acetoxybenzoic acid and 6-acetoxy-2-naphthoic acid. Within a range of... 

Nevertheless remarkable is the failure of the diphenols 10a and 10b to yield LC-homo PEIs. Computer modelling of 9b, 10a and 10b in their energy minimum conformations (Fig. 5) revealed the following differences. The diphenyl ether moiety has a relatively wide bond angle (124 1°) and requires little activation energy to adopt a nearly coplanar conformation of the phenylene rings. 

---