Phase diagram, sheared morphologies, polymer

The effect of a simple shear flow on the phase behavior and morphology was investigated with the use of a parallel-plate apparatus (Fig. 8.4, Madbouly et al. 1999a) for some polymer mixtures poly(methyl methacrylate) (PMMA)/ poly(styrene-co-acrylonitrile) (SAN-29.5) and polystyrene (PS)/poly(vinyl methyl ether) (PVME), which have an LCST-type phase diagram PS/PMMA, which has a UCST-type phase diagram and polycarbonate (PC)/SAN and nylon4, 6(PA4,6)/ poly(phenylene sulfide) (PPS), which are immiscible in the whole measurable region under the quiescent state. 

Experimental phase diagrams for amorphous block copolymers were explored by Khandpur and co-workers (29). First, low-frequency isochronal shear modulus-temperature curves were developed on a series of polyiso-prene-h/ocA -polystyrene polymers to guide the selection of temperatures for the transmission electron microscopy and SAXS experiments to follow see Figure 13.14 (29). Both order-order (OOT) and ODT transitions were iden-tihed. The OOT are marked by open arrows, while the ODT are shown by hlled arrows. Since the ODT occurs as the temperature is raised, an upper critical solution temperature is indicated, much more frequent with block copolymers than with polymer blends. The regions marked A, B, C, and D denote lamellar, bi-continuous, cylindrical, and perforated layered microstructures, respectively. The changes in morphology are driven by the temperature dependence of Xn,... 

---